Lorentz Transmission Electron Microscopy Investigation of Magnetically Patterned Co/pt Multilayers

The switching behavior of magnetic patterns prepared by ion irradiation was investigated. Co/Pt multilayers with perpendicular anisotropy and large out-of-plane coercivities 5-6 kOe were grown on electron transparent SiN windows. Regularly spaced 1 micron sized regions, were magnetically pattered via ion beam irradiation through a stencil mask. Lorentz TEM was used to observe in-situ magnetization reversal processes of irradiated regions under well-defined applied magnetic fields. When the in-plane field was increased, domain wall motion was observed, resulting in the alignment of the patterns with the direction of the applied field. The switching mechanism of the in-plane patterns was by domain wall motion.