Bauxite-supported Transition Metal Oxides: Promising Low-temperature and SO2-tolerant Catalysts for Selective Catalytic Reduction of NOx
نویسندگان
چکیده
In order to develop low-temperature (below 200 °C) and SO2-tolerant catalysts for selective catalytic reduction (SCR) of NOx, a series of cheap M/bauxite (M = Mn, Ni and Cu) catalysts were prepared using bauxite as a support. Their SCR performances are much superior to typical V2O5/TiO2, the addition of M into bauxite results in significant promotion of NOx removal efficiency, especially at low temperature. Among the catalysts, Cu/bauxite exhibits wide temperature window over 50-400 °C, strong resistance against SO2 and H2O as well as good regeneration ability in SCR of NOx. NOx conversion is more than 80% at 50-200 °C, and N2 selectivity is more than 98%. Cu/bauxite can serve as a promising catalyst in SCR of NOx.
منابع مشابه
Optimization and Modeling of CuOx/OMWNT’s for Catalytic Reduction of Nitrogen Oxides by Response Surface Methodology
A series of copper oxide (CuOx) catalysts supported by oxidized multi-walled carbon nanotubes (OMWNT’s) were prepared by the wet impregnation method for the low temperature (200 °C) selective catalytic reduction of nitrogen oxides (NOx) using NH3 as a reductant agent in the presence of excess oxygen. These catalysts were characterized by FTIR, XRD, SEM-EDS, and H2-TPR meth...
متن کاملLow temperature selective catalytic reduction of NOx with NH3 over Mn-based catalyst: A review
The removals of NOx by catalytic technology at low temperatures (100–300 °C) for industrial flue gas treatment have received increasing attention. However, the development of low temperature catalysts for selective catalytic reduction (SCR) of NOx with ammonia is still a challenge especially in the presence of SO2. The current status of using Mn-based catalysts for low temperature SCR of NOx wi...
متن کاملSulfur and Water Resistance of Mn-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOx: A Review
Selective catalytic reduction (SCR) with NH3 is the most efficient and economic flue gas denitrification technology developed to date. Due to its high low-temperature catalytic activity, Mn-based catalysts present a great prospect for application in SCR de-NOx at low temperatures. However, overcoming the poor resistance of Mn-based catalysts to H2O and SO2 poison is still a challenge. This pape...
متن کاملMolecular structure–reactivity relationships for the oxidation of sulfur dioxide over supported metal oxide catalysts
The catalytic oxidation of sulfur dioxide to sulfur trioxide over several binary (MxOy/TiO2) and ternary (V2O5/MXOY/TiO2) supported metal oxide catalysts was systematically investigated. The supported metal oxide components were essentially 100% dispersed as surface metal oxide species, as confirmed by Raman spectroscopy characterization. The sulfur dioxide oxidation turnover frequencies of the...
متن کاملLarge-scale growth of hierarchical transition-metal vanadate nanosheets on metal meshes as monolith catalysts for De-NO(x) reaction.
A facile method is developed for the large-scale growth of hierarchical transition-metal (Cu, Fe, and Ni) vanadate nanosheets on corresponding metal mesh as supports. The hierarchical transition-metal vanadate nanosheets were in situ grown on the metal meshes through an orientational etching process and simultaneous nucleation and growth process. Interestingly, the morphologies of the vanadate ...
متن کامل