Polyvinyl Chloride / Attapulgite / Micro-crystalline Cellulose (MCC) Composites Preparation and Analysis of the Role of MCC as a Compatibilizer

نویسندگان

  • Bo Wang
  • Hai-Rong Zhang
  • Chao Huang
  • Xue-Fang Chen
  • Si-Lan Shi
  • Lian Xiong
  • Jun Luo
  • Xin-De Chen
چکیده

To improve the performance of polyvinyl chloride (PVC), composites incorporating polyvinyl chloride (PVC), attapulgite nanoparticles (ANPs), and microcrystalline cellulose (MCC) were successfully prepared. The composites had higher vicat softening temperatures (VSTs) and the MCC had a great influence on mechanical properties of the composites. When MCC was added from 0 to 5 per hundred parts of PVC (phr), the mechanical properties of the composites increased, but the mechanical properties of the composites decreased when the MCC was more than 5 phr. The tensile breaking stress, tensile strength, and impact strength were maximized with increases of 19.76 N (4.1%), 29.66 MPa (15.5%), and 13.8 MPa (7%) when 5 phr MCC was added. Infrared spectral analysis indicated that MCC and ANPs were present in the composites. Scanning electron microscopy showed that the composites system was distributed into two phases, which indicated that MCC in composites was dissolved in the PVC matrix, and some of MCC coated the surface of ANPs as a compatibilizer. Overall, this study provided a promising method for PVC modification to improve its performance.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Preparation of Micro-Crystalline Cellulose-Reinforced Polyacrylic Acid Hydrogel and its Application in Paper/Polyacrylic Acid Composites

Paper/polyacrylic acid (PAA) composites were prepared using a microcrystalline cellulose (MCC)-reinforced PAA hydrogel. The MCC-reinforced PAA hydrogel was prepared by in-situ UV light-induced polymerization of acrylic acid in the presence of MCC. The experimental results showed that the presence of MCC improved the water absorption capacity of the resulting PAA hydrogel. The addition of 1 wt% ...

متن کامل

Preparation and Properties of a Novel Microcrystalline Cellulose-Filled Composites Based on Polyamide 6/High-Density Polyethylene

In the present study, lithium chloride (LiCl) was utilized as a modifier to reduce the melting point of polyamide 6 (PA6), and then 15 wt % microcrystalline cellulose (MCC) was compounded with low melting point PA6/high-density polyethylene (HDPE) by hot pressing. Crystallization analysis revealed that as little as 3 wt % LiCl transformed the crystallographic forms of PA6 from semi-crystalline ...

متن کامل

Properties of polylactic acid composites reinforced with oil palm biomass microcrystalline cellulose.

In this work, polylactic acid (PLA) composites filled with microcrystalline cellulose (MCC) from oil palm biomass were successfully prepared through solution casting. Fourier transform infrared (FT-IR) spectroscopy indicates that there are no significant changes in the peak positions, suggesting that incorporation of MCC in PLA did not result in any significant change in chemical structure of P...

متن کامل

Characterization of cellulose II nanoparticles regenerated from 1-butyl-3-methylimidazolium chloride.

Regenerated cellulose nanoparticles (RCNs) including both elongated fiber and spherical structures were prepared from microcrystalline cellulose (MCC) and cotton using 1-butyl-3-methylimidazolium chloride followed by high-pressure homogenization. The crystalline structure of RCNs was cellulose II in contrast to the cellulose I form of the starting materials. Also, the RCNs have decreased crysta...

متن کامل

Preparation and Evaluation of Multi-Particulate System (Pellets) of Prasugrel Hydrochloride

Multiparticulate systems (pellets) of prasugrel hydrochloride were prepared by extrusion spheronization method using MCC (micro crystalline cellulose). Optimum spheronization time and method of drying were selected as the process parameters for the preparation of final batches. Various pellet properties were evaluated like size & shape analysis, flow properties, bulk & tapped density, friabilit...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2015