A new restriction effect of hard templates for the shrinkage of mesoporous polymer during carbonization.
نویسندگان
چکیده
A new restriction effect of hard templates for the shrinkage of mesoporous polymer results in anomalous increase of the mesopore size during carbonization.
منابع مشابه
Highly Mesoporous Carbons Obtained Using a Dynamic Template Method
New nanoporous carbons with extremely high mesopore volumes and surface areas were obtained using mesoporous silica with a 3-D wormhole porous framework as templates. Mesoporous silica was synthesized following the literature described methods. Polystyrene sulfonic acid-based organic salts were used as carbon precursors. To evaluate the effect of sodium on porosity development silica matrices w...
متن کاملTen Years of Research on Ordered Mesoporous Carbons: Major Advances in Synthesis, Properties and Potential Applications
About ten years ago Ryoo and co-workers [1,2] reported the hard-templating (HT) synthesis of ordered mesoporous carbons (OMCs) by using ordered mesoporous silicas (OMSs) as hard templates. Five years afterward the soft-templating (ST) synthesis of OMCs has been discovered [3-6]. Significant progress has been made in both hardand soft-templating synthesis of OMCs [7-10]. Major advances in the sy...
متن کاملMesoporous N-doped carbons prepared with thermally removable nanoparticle templates: an efficient electrocatalyst for oxygen reduction reaction.
Thermally removable nanoparticle templates were used for the fabrication of self-supported N-doped mesoporous carbons with a trace amount of Fe (Fe-N/C). Experimentally Fe-N/C was prepared by pyrolysis of poly(2-fluoroaniline) (P2FANI) containing a number of FeO(OH) nanorods that were prepared by a one-pot hydrothermal synthesis and homogeneously distributed within the polymer matrix. The FeO(O...
متن کاملMesoporous graphitic carbon nanodisks fabricated via catalytic carbonization of coordination polymers.
Mesoporous graphitic carbon nanodisks with hierarchical porous structure, facilely fabricated by catalytic carbonization of iron-based coordination polymer nanodisks, exhibit high capacitance even at high scan rates as electrode materials for electrochemical double layer capacitors.
متن کاملHierarchical Phenolic Resin-based Carbons with High Surface Area and Pore Volume Obtained by Soft-templating and Activation
Introduction Advanced applications often require carbons with high surface area and hierarchical porous structures. In response to this demand some efforts have been undertaken to create materials, which effectively combine the properties of both activated carbons (high surface area) and ordered mesoporous carbons (tunable and well-developed porosity). While there are activation methods, which ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 33 شماره
صفحات -
تاریخ انتشار 2009