Crystallization Process in Porous and Nonporous Vycor Glass
نویسندگان
چکیده
Three stages of thermal and chemical processing of Vycor glass were carried out. Raw material, the glass with small and big pores was studied. In each stage of study various crystallinity degrees of investigated material were obtained. The relation between crystallinity degree and the intensity of o-Ps components was determined. In nonporous material a high correlation between o-Ps intensity and crystallinity degree was found. In porous material the decrease in total o-Ps intensity can be a measure of the crystallinity degree.
منابع مشابه
Three - Quantum Annihilation in Porous Vycor Glass
f = τoPs/τoPs(vac), (1) where τoPs and τoPs(vac) are o-Ps lifetime in the sample and in vacuum, respectively. Three-quantum annihilation studies become competitive to the traditional positron annihilation lifetime spectrometry (PALS), in particular in the relation to porous media and positron beam technique [1]. Below we compare the results of estimation of 3γ intensity obtained by several clas...
متن کاملAddition of Alumina to Nanoporous Calcium Titanium Phosphate Glass-Ceramics and its Effects on Crystallization Behavior
Microporous Calcium Titanium Phosphate glass-ceramics have many uses in high-tech industries. For example, they have applications in catalysts industry. In this study, different molar percentages of alumina were added to a glass with P2O5 30, CaO 45, TiO2 25 (mol%) composition. The samples were melted at 1350°C and crystallization heat treatment was performed on...
متن کاملDetermination of the Nucleation and Crystallization Parameters for Making Nanoporous Titanium Phosphate Glass-ceramics
Nanoporous glass-ceramics were prepared with composition 45CaO-25TiO2-35P2O5 (mol%). Two molar percent of Na2O was added as a flux to the composition. With the aforementioned composition, glass melted and crystallized into glass-ceramics containing β-Ca3(PO4)2 and CaTi4(PO4)6 as the main phases. The differential thermal analysis (DTA) was conducted to determine the suitable temperatures f...
متن کاملOn the Formation of Nanobubbles in Vycor Porous Glass during the Desorption of Halogenated Hydrocarbons
Vycor porous glass has long served as a model mesoporous material. During the physical adsorption of halogenated hydrocarbon vapours, such as dibromomethane, the adsorption isotherm exhibits an hysteresis loop; a gradual ascent is observed at higher pressures during adsorption, and a sharp drop is observed at lower pressures during desorption. For fully wetting fluids, an early hypothesis attri...
متن کاملAdsorption of water on porous Vycor glass studied by ellipsometry.
The variation of the optical properties of porous Vycor glass (Corning, Model 7930) under different relative-humidity conditions was studied. The adsorption of water into the glass pores was investigated with spectroscopic ellipsometry. The change of the refractive index was Deltan approximately 0.04 between 5% and 90% relative humidity. A linear relation between the ellipsometer parameter tan ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2005