Adsorption and Desorption Mechanisms of Methylene Blue Removal with Iron-Oxide Coated Porous Ceramic Filter
نویسندگان
چکیده
Adsorption and desorption mechanisms of methylene blue (MB) removal with iron-oxide coated porous ceramics filter (IOCPCF) were investigated in batch and column mode. The results revealed that MB removal mechanisms included physical adsorption and chemical adsorption, of which chemical adsorption by surface ligand complex reaction played a dominant role after infrared spectrum analysis. Recycling agents were selected from dilute nitric acid (pH=3), sodium hydroxide solution (pH=12) and distilled water. Among three agents, dilute metric acid (pH=3) was the best recycling agent. Regeneration rate of IOCPCF arrived at 82.56% at batch adsorption and regeneration was finished in 75min at column adsorption. Adsorption-desorption cycles of IOCPCF after batch and column adsorption were four and three times, respectively. Further, compared with fresh IOCPCF, MB removal rate with these desorbed IOCPCF adsorption only slightly decreased, which suggested that IOCPCF should be used repeatedly.
منابع مشابه
Removal of Fe2+ from Aqueous Solution Using Manganese Oxide Coated Zeolite and Iron Oxide Coated Zeolite
The adsorption of Fe2+ by the manganese oxide coated zeolite (MOCZ) and iron oxide coated zeolite (FOCZ) was studied. Surface properties of adsorbents have been investigated for monitoring their changes and morphology for both of the MOCZ and FOCZ. Main variables namely; contact time, pH, initial concentration of Fe2+, size and dosage of adsorbent have been optimized, and the results contrasted...
متن کاملSynthesis and characterization of poly (AAm-co-AAc)/NaA nanocomposite and removal of methylene blue with it
The nanocomposites of poly (Acryl amide-co-Acrylic acid) with different contents of NaAzeolite were prepared using ammonium persulfate as an initiator and N, N′-methylenebisacrylamide as the crosslinker. The morphology was characterized by SEM and the structure ofnanocomposite materials was studied with XRD and FT-IR that showed the interaction betweenporous materials and poly (AAm-co-Aac). The...
متن کاملSynthesis of activated carbon/zinc oxide nanocomposite from rapeseed plant waste by green chemistry method, evaluation of its performance in Methylene Blue pigment removal and optimization of influencing parameters using design expert
Background and Objective: Due to the water shortages and the presence of industrial pollutants in water resources, wastewater treatment, especially colored wastewater, is essential. The aim of this study was to treat wastewater containing Methylene Blue dye using activated carbon nanocomposite/zinc oxide nanoparticles (ZnO/AC) obtained from canola oil waste by green method. Materials and Metho...
متن کاملRemoval of methylene blue dye by application of polyaniline nano composite from aqueous solutions
This paper deals with application of polyaniline coated on wood sawdust for removal ofmethylene blue (MB) dye from aqueous solutions. Polyaniline coated onto sawdust (termedas PAn/SD) was prepared via direct chemical polymerization onto sawdust which waspreviously soaked in the monomer (aniline) solution in acidic (HC1) media. Adsorptionexperiments were carried out using batch system. The effec...
متن کاملApplication of Copper Vanadate Nanoparticles for Removal of Methylene Blue from Aqueous Solution: Kinetics, Equilibrium, and Thermodynamic Studies
Copper vanadate nanoparticles were synthesized by a simple coprecipitation method in an aqueous medium and the products were used as adsorbents for eliminating methylene blue (MB) from water. The structure and morphology of the produced nanoparticles were evaluated through X-Ray Diffraction (XRD) and Field Emission Scanning Electron Microscopy (FESEM) analysis. The results...
متن کامل