High temperature fatigue crack growth of Haynes 230 - 1-s2.0-S1044580312002665-main

نویسندگان

  • Garrett J. Pataky
  • Huseyin Sehitoglu
  • Hans J. Maier
چکیده

Article history: Received 5 July 2012 Received in revised form 25 September 2012 Accepted 29 September 2012 The fatigue crack growth of the nickel-based superalloy Haynes 230 was investigated at room temperature and 900 °C using digital image correlation (DIC). As expected, the crack growth rates at high temperature were much faster than at room temperature. However, the crack closure levels, which were determined using digital image correlation analysis techniques, were found to be similar for the two cases studied. DIC strain fields and the corresponding plastic zone sizes were compared between the two cases. From these strain fields, the slip irreversibility, the difference between forward and reversed strains at the crack tip, was quantitatively measured. The high temperature case had an order of magnitude higher amount of slip irreversibility. Slip irreversibility measurements were determined to be an effective method to compare fatigue crack growth of cases with differing temperatures. © 2012 Elsevier Inc. All rights reserved.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Fatigue crack growth in Haynes 230 single crystals: an analysis with digital image correlation

Fatigue crack growth was investigated in Haynes 230, a nickel-based superalloy. Anisotropic stress intensity factors were calculated with a least squares algorithm using the displacements obtained from digital image correlation. Crack opening/sliding levels were measured by analysing the relative displacement of crack flanks. Reversed crack tip plastic zones were calculated adopting an anisotro...

متن کامل

Near-tip closure and cyclic plasticity in Ni-based single crystals

Fatigue crack growth was investigated in a 001 1⁄2 oriented single crystal specimen, made of a Ni-based superalloy, Haynes 230. Crack propagation was characterized with digital image correlation: crack closure, measured by analyzing the relative displacements of crack flanks, showed closure levels much lower than polycrystal alloys. Reversed plastic zones were calculated from regressed stress i...

متن کامل

The Fracture Mechanics Concept of Creep and Creep/Fatigue Crack Growth in Life Assessment

There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...

متن کامل

HIGH-TEMPERATURE FRACTURE AND FATIGUE RESISTANCE OF A DUCTILE b-TiNb REINFORCED g-TiAl INTERMETALLIC COMPOSITE

ÐThe high-temperature fatigue-crack propagation and fracture resistance of a model g-TiAl intermetallic composite reinforced with 20 vol.% ductile b-TiNb particles is examined at elevated temperatures of 650 and 8008C and compared with behavior at room temperature. TiNb reinforcements are found to enhance the fracture toughness of g-TiAl, even at high temperatures, from about 12 to 040 MPa m, a...

متن کامل

MICROSTRUCTURE VARIATION EFFECTS ON ROOM TEMPERATURE FATIGUE THRESHOLDS AND CRACK PROPAGATION IN UDIMET 720Li Ni-BASE SUPERALLOY

An assessment of the effects of microstructure on room temperature fatigue threshold and crack propagation behaviour has been carried out on microstructural variants of U720Li, i.e. as-received U720Li, U720Li-LG (large grain variant) and U720Li-LP (large intragranular coherent γ′ variant). Fatigue tests were carried out at room temperature using a 20Hz sinusoidal cycling waveform at an Rratio=0...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013