Effect of Filler Size and Temperature on Packing Stress and Viscosity of Resin-composites
نویسندگان
چکیده
UNLABELLED The objective of this study was to investigate the effect of filler size on the packing stress and viscosity of uncured resin-composite at 23 °C and 37 °C. A precision instrument used was designed upon the penetrometer principle. Eight resin-composite materials were tested. Packing-stress ranged from 2.60 to 0.43 MPa and viscosity ranged from 2.88 to 0.02 MPa.s at 23 °C. Values for both properties were reduced significantly at 37 °C. Statistical analysis, by ANOVA and post hoc methods, were carried out to check any significant differences between materials tested (P < 0.05). CONCLUSIONS Filler size and distribution will affect the viscosity and packing of resin-composites during cavity placement.
منابع مشابه
Rheological properties of resin composites according to variations in composition and temperature.
OBJECTIVE To study the effect of compositional variables and temperature (25°C and 37°C) on the rheological properties of contemporary resin composites. METHODS Fourteen commercial resin composites with different resin matrices of Bis-GMA and TEGDMA, different filler loading (41-65, v/v) and particle sizes (ranging 5nm to 20μm) were studied using a parallel plate rheometer. Shear sweep measur...
متن کاملHeat Effect on Viscosity and Curing of Light-Cured Dental Resin and Mechanical Strength of Conventional Dental Composites
Dimethacrylate polymers and silica are most commonly used as matrix resins and fillers for dental composites. Bis-GMA, UDMA are used as base monomers and TEGDMA as a diluent monomer for dental resin preparation. Pure UDMA, mixtures of UDMA:TEGDMA and Bis-GMA:TEGDMA 50:50 and 75:25 were mixed with silanized silica at compositions of monomer:fillers 30:70 and 40:60 (weight ratio). Heat curing of ...
متن کاملBulkfill flowable composite resins – A review
Flowable composite resins are widely used in clinical practice. Bulk Fill flowable resins with improved mechanical and chemical characteristics have recently been introduced. These composites are low-viscosity materials with the reduced percentage of inorganic filler particles and higher amount of resinous components. Consequently, the polymerization process leads to volumetric contraction, but...
متن کاملEffect of filler size and filler loading on wear of experimental flowable resin composites
The relationship between wear resistance and filler size or filler loading was clarified for the universal resin composite; however, their relationship in flowable resin composites has not been clarified. The purpose of this study was to investigate the effect of filler size and filler loading on wear of experimental flowable resin composites by using a cyclic loading device. Nine experimental ...
متن کاملبررسی اثر نوع فیلر بر سایش سه جزئی کامپوزیت دندانی
Statement of Problem: The relatively poor wear resistance of dental composite in stress bearing posterior situations has restricted wider clinical application of this restorative material. Purpose: The aim of this study was to evaluate the three body abrasive wear of a dental composite based on a new filler (leucite: KAl Si2O6) and to compare it with the wear resistance of a composite based on ...