Determination of Screw Withdrawal Strength of Heat- Treated and Reinforced Laminated Veneer Lumber
نویسنده
چکیده
The withdrawal resistance of screws in heat-treated and reinforced laminated veneer lumber (RLVL) was determined in the radial, tangential, and transverse directions. For this reason, laminated veneer lumber (LVL) and RLVL with carbon fibers were produced from heattreated oak (Quercus petraea (Liebl.)) veneers using phenol formaldehyde as the adhesive. Wood samples were heat-treated at 140, 170, 200, and 230 °C for 2 h. According to the results of the study, screw withdrawal strength values of LVL increased for heat-treated samples at 140 °C, but decreased at 170, 200, and 230 °C. However, in all groups, the screw withdrawal strength values of the RLVL were higher than those of the LVL. The highest screw withdrawal strength values were identified in the tangential direction, and the lowest were in the transverse directions. Carbon fiber can be used between the heat-treated wood veneers to provide sufficient screw withdrawal strength for use in many different industries.
منابع مشابه
SOME TECHNOLOGICAL PROPERTIES OF LAMINATED VENEER LUMBER PRODUCED WITH FAST-GROWING Poplar AND Eucalyptus
Fast-growing tree species are important due to their short growth time before they are harvested. Both the Poplar and Eucalyptus species are fast-growing trees. These two species have been cultivated in many parts of the world, and they are used in several ways, including in the pulp and paper industry, as wood-based panels, and as structural composite lumber. In this study, laminated veneer lu...
متن کاملT He Pqssmlllty of Lamlna11nc Lumber from Sliced or Forest Products Journal
By the lamination process evaluated, 60 percent of total 108 volume ended as kiln-dry, end-trimmed, sized, salable 2 by 4's-approximately 50 percent more than that achieved by conventional bandsawing of matched lop. Moreover, modulus of elasticity of the laminated 2 by 4's (adjusted to 12 percent moisture content) averaged 1,950,000 psi compared to 1,790,000 for the sawn 2 by 4's. Allowable fib...
متن کاملMechanical Properties Analysis and Reliability Assessment of Laminated Veneer Lumber (lvl) Having Different Patterns of Assembly
Laminated Veneer Lumber (LVL) panels made from poplar (Populus ussuriensis Kom.) and birch (Betula platyphylla Suk.) veneers were tested for mechanical properties. The effects of the assembly pattern on the modulus of elasticity (MOE) and modulus of rupture (MOR) of the LVL with vertical load testing were investigated. Three analytical methods were used: composite material mechanics, computer s...
متن کاملEffect of Boric Acid Treatment on Mechanical Properties of Laminated Beech Veneer Lumber
In spite of many alternative materials like iron, plastic, and concrete, which can be used instead of solid wood in different areas, wood remains superior as a natural engineering material. Due to depletion of forest resources, forest products industries are faced with a crisis in obtaining suitable raw materials in suffi cient amount. Therefore, layered composite materials like vertically and ...
متن کاملThe Effect of Joint Form and Parameter Values on Mechanical Properties of Bamboo-Bundle Laminated Veneer Lumber (BLVL)
Bamboo-bundle laminated veneer lumber (BLVL) was produced by joint lengthening technology. The objective of this study was to evaluate the effect of joint form and the values of key parameters on mechanical properties of BLVL. Two joint forms, i.e., finger joint and scarf joint, and two corresponding joint parameters, i.e., finger length and scarf angle, were investigated in laminates. The resu...