Improvement of the electron collection efficiency in porous hematite using a thin iron oxide underlayer: towards efficient all-iron based photoelectrodes.
نویسندگان
چکیده
Different approaches have been explored to increase the water oxidation activity of nanostructured hematite (α-Fe2O3) photoanodes, including doping with various elements, surface functionalization with both oxygen evolving catalysts (OEC) and functional overlayers and, more recently, the introduction of ultrathin oxide underlayers as tunneling back contacts. Inspired by this latter strategy, we present here a photoanode design with a nanometric spin-coated iron oxide underlayer coupled with a mesoporous hematite film deposited by electrophoresis. The electrodes equipped with the thin underlayer exhibit a four-fold improvement in photoactivity over the simple hematite porous film, reaching a stable photocurrent density of ca. 1 mA cm(-2) at 0.65 V versus the saturated calomel electrode (SCE) at pH 13.3 (NaOH 0.1 M) under air mass (AM) 1.5G illumination. A further improvement to 1.5 mA cm(-2) is observed after decoration of the hematite surface with a Fe(iii)-OEC. These results demonstrate that by combining different iron oxide morphologies, it is possible to improve the selectivity of the interfaces towards both electron collection at the back contact and hole transfer to the electrolyte, obtaining an efficient all-iron based photoelectrode entirely realized with simple wet solution scalable procedures.
منابع مشابه
Synthesis of Iron Oxide Nanoparticles using Borohydride Reduction
Iron oxide (Fe2O3) nanoparticles were synthesized by a simple approach using sodium borohydride (NaBH4) and Iron chloride hexahydrate (FeCl3.6H2O). Their physicochemical properties were characterized by high resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and electron dispersive spectroscopy (EDS). XRD pattern showed that the iron...
متن کاملSynthesis of Iron Oxide Nanoparticles using Borohydride Reduction
Iron oxide (Fe2O3) nanoparticles were synthesized by a simple approach using sodium borohydride (NaBH4) and Iron chloride hexahydrate (FeCl3.6H2O). Their physicochemical properties were characterized by high resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and electron dispersive spectroscopy (EDS). XRD pattern showed that the iron...
متن کاملParticle size and kind of mica in synthesis of nontoxic bronze and gold pearlescent pigments based on nanoencapsulated hematite
Nano-encapsulated iron oxide in Zirconium oxide-coated mica pigments are thermally stable,innocuous to human health, non-combustible, and they do not conduct electricity. They could beapplied in several industries such as thermoplastics, cosmetics, food packaging, children toys, paints,automobiles coating, security purposes, and banknotes. Nowadays, they are highly desirable inceramic decoratio...
متن کاملRECOVERY OF IRON FROM LOW-GRADE HEMATITE ORE USING COAL-BASED DIRECT REDUCTION FOLLOWED BY MAGNETIC SEPARATION
In the present work, iron recovery from a low-grade hematite ore (containing less than 40% iron), which is not applicable in common methods of ironmaking, was studied. Non-coking coal was used as reducing agent. Reduction experiments were performed under various coal to hematite ratios and temperatures. Reduction degree was calculated using the gravimetric method. Reduced samples were subjected...
متن کاملElectrochemical properties of iron oxide nanoparticles as an anode for Li-ion batteries
The synthesis of iron oxide nano-particles by direct thermal decomposition was studied. Simultaneous thermal analysis and Fourier transform infrared spectroscopy results confirmed the formation of iron-urea complex, and disclosed iron oxide formation mechanism. Calcination of the iron-urea complex at 200°C and 250°C for 2 hrs. resulted in the formation of maghemite along with hematite as a seco...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Physical chemistry chemical physics : PCCP
دوره 17 44 شماره
صفحات -
تاریخ انتشار 2015