Synthesis of dimethacryloxy ethyl-1,1,6,6-tetrahydro-perfluorohexamethylene-1,6-dicarbamate as dental base monomers and the mechanical properties of the copolymers of the monomer and methyl methacrylate.

To recognize good mechanical properties and water-resistance of a dental resin, dimethacryloxyethyl-1,1,6,6-tetrahydro-perfluoro-hexamethylene-1,6-dicarbamate (FDMHD) was newly synthesized. FDMHD initially was a white powder with m.p. 98.5-99.5°C. The copolymers of FDMHD and methyl methacrylate (MMA), FDMHD/MMA copolymers, were prepared to estimate the basic properties for dental resin materials. The compressive strength of FDMHD/MMA copolymers was almost the same compared with those of the copolymers of Bis-GMA or dimethacryloxyethyl-hexamethylene-1,6-carbamate (DMHD) and MMA. The bending, tensile, diametral tensile, impact strength and toughness of FDMHD/MMA copolymers containing 10.4 mol% FDMHD were higher than those of Bis-GMA/MMA copolymer, and the water sorption of FDMHD/MMA copolymers was lower than those of DMHD/MMA copolymers.