Size-Controlled Synthesis of Colloidal Gold Nanoparticles at Room Temperature Under the Influence of Glow Discharge
نویسندگان
چکیده
Highly dispersed colloidal gold (Au) nanoparticles were synthesized at room temperature using glow discharge plasma within only 5 min. The prepared Au colloids were characterized with UV-visible absorption spectra (UV-vis), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM) equipped with an energy dispersion X-ray spectrometer (EDX). UV-vis, XPS and EDX results confirmed that Au3+ ions in HAuCl4 solution could be effectively reduced into the metallic state at room temperature with the glow discharge plasma. TEM images showed that Au nanoparticles were highly dispersed. The size of colloidal Au nanoparticles could be easily tuned in the nanometer range by adjusting the initial concentration of HAuCl4 solution. Moreover, the as-synthesized Au colloids (dav = 3.64 nm) exhibited good catalytic activity for glucose oxidation. The nucleation and growth of colloidal Au particles under the influence of the plasma was closely related with the high-energy electrons generated by glow discharge plasma.
منابع مشابه
Synthesis of AuPd alloyed nanoparticles via room-temperature electron reduction with argon glow discharge as electron source
Argon glow discharge has been employed as a cheap, environmentally friendly, and convenient electron source for simultaneous reduction of HAuCl4 and PdCl2 on the anodic aluminum oxide (AAO) substrate. The thermal imaging confirms that the synthesis is operated at room temperature. The reduction is conducted with a short time (30 min) under the pressure of approximately 100 Pa. This room-tempera...
متن کاملA Facile pH Controlled Citrate-Based Reduction Method for Gold Nanoparticle Synthesis at Room Temperature
The synthesis of gold nanoparticles using citrate reduction process has been revisited. A simplified room temperature approach to standard Turkevich synthesis is employed to obtain fairly monodisperse gold nanoparticles. The role of initial pH alongside the concentration ratio of reactants is explored for the size control of Au nanoparticles. The particle size distribution has been investigated...
متن کاملApplication of Molybdophosphoric Acid as Reducing Agent/ Stabilizer in the Synthesis of Gold Nanoparticles under UV Irradiation
In this paper, we have described the size-controlled synthesis of gold nanoparticles based on the reduction of Au3+ (HAuCl4 ) using molybdophosphoric acid (H3[PMo12O40 ], HPMo) under UV-irradiation. In the process, HPMo plays the role of photocatalyst, reducing agent and stabilizer and propan-2-ol acts as a sacrificial agent. This method allows the synthesis of uniform hexagonal nanoparticles w...
متن کاملSynthesis of Silver Nanoparticles Using Silybum Marianum Seed Extract
Green synthesis of nanoparticles, as fundamental building blocks of nanotechnology, has recently attracted considerable attention. Silver nanoparticles have unique physiochemical, biological and environmental properties which make them useful in a wide range of applications. In the present paper we report our research results on biosynthesis of silver nanoparticles from silver precursor usin...
متن کاملStructural and Optical Behavior of Cu Doped Au Nanoparticles Synthesized by Wet-Chemical Method
The nanoparticles of gold doped with various percentage of copper (Cu 10%, 25%, 75%) were synthesized by wet-chemical method at room temperature. Copper (II) sulfate and gold (III) chloride trihydride was taken as the metal precursor and ascorbic acid as a reducing agent and anhydride maleic as surfactant. The reaction is performed with high-speed stirring at room temperature under nitrogen atm...
متن کامل