Wear and Mechanical Properties of Nodular Iron Modified with Copper
نویسندگان
چکیده
In this research (using induction furnace process) nodular iron with three different percentages of copper (residual, 0.5% and 1,2%) was obtained. Chemical analysis was performed by mass spectrometry and microstructures were characterized by Optical Microscopy (ASTM E3) and Scanning Electron Microscopy (SEM). The study of mechanical behavior was carried out in a mechanical test machine (ASTM E8) and a Pin on disk tribometer (ASTM G99) was used to assess wear resistance. It is observed that the dissolution of copper in crystal lattice increases the pearlite structure improving the wear and hardness behavior, but producing a contrary effect on the energy absorption. Keywords—Ferritic and perlite structure, mechanical properties, nodular iron, wear.
منابع مشابه
Investigating the Effect of Titanium Addition on the Microstructure and Mechanical Properties of Ni-Hard 4 Cast Iron
Ni-Hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. In this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the Ni-hard 4 cast iron with the nominal composition of Si= 1.5%, Mn=0.5%, C=3%, P=0.05%, S= 0.05%, Mo= 0....
متن کاملInvestigating the Effect of Titanium Addition on the Microstructure and Mechanical Properties of Ni-Hard 4 Cast Iron
Ni-Hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. In this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the Ni-hard 4 cast iron with the nominal composition of Si= 1.5%, Mn=0.5%, C=3%, P=0.05%, S= 0.05%, Mo= 0....
متن کاملThe Effect of Heat Treatment Cycle on Microstructure and Mechanical Properties of Austempered Ductile Iron with Various Copper Contents.
متن کامل
The Effect of Heat Treatment Cycle on Microstructure and Mechanical Properties of Austempered Ductile Iron with Various Copper Contents.
متن کامل
Structural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کامل