Comparison of Medium Manganese Steel and Q345 Steel on Corrosion Behavior in a 3.5 wt % NaCl Solution
نویسندگان
چکیده
A cyclic wet/dry accelerated corrosion test was used to compare the corrosion behavior of medium-Mn steel and Q345 steel. In terms of scanning electron microscope (SEM), using X-ray diffraction (XRD), electron probe microanalysis (EPMA), X-ray photoelectron spectroscopy (XPS), and analysis of the corrosion process, the results showed that the medium-Mn steel did not exhibit higher corrosion resistance than Q345 steel due to the greater content of Mn-rich compounds in the rust layer. Moreover, the effect of a small amount of anti-corrosion elements in medium-manganese steel can regulate the corrosion rate. The conceptual model of the corrosion process of the medium-Mn steel in a 3.5 wt % NaCl solution is proposed.
منابع مشابه
Turmeric extract as a biocompatible inhibitor of mild steel corrosion in 3.5% NaCl solution
Corrosion inhibitory impacts of turmeric with concentrations of 200-800 ppm on the electrochemical behavior of mild steel were studied in the medium of NaCl 3.5% using several techniques such as electrochemical impedance spectroscopy (EIS) and polarization. Scanning electron microscopy (SEM) was used for analyzing the surface of mild steel after 24 hours of immersion in the electrolyte solution...
متن کاملEffect of ageing heat treatment on corrosion behaviorof 17-4 PH stainless steel in 3.5% NaCl
The 17-4PH alloy is a martensitic stainless steel with 3–5 wt% Cu, strengthened by the precipitation hardening. Due to excellent mechanical properties, corrosion resistance and ease of heat treatment, this alloy has unique applications in nuclear power plants and marine constructions. In this paper, the influence of ageing heat treatment, solution annealing followed by ageing at 480, 550 and 62...
متن کاملThe Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution
One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...
متن کاملQuantum chemical studies on adsorption of imidazole derivatives as corrosion inhibitors for mild steel in 3.5 NaCl solution
Adsorption of benzimidazole, 2-methylbenzimidazole and 2-aminobenzimidazole on mild steel in 3.5 NaCl solution was studied using density function theory DFT calculations. In this regard, charge transfer resistance Rct and double layer capacitance Cdl obtained by electrochemical impedance spectroscopy EIS were used to calculate surface coverage and to build prediction models. When prediction mod...
متن کاملElectrochemical Characterizations of Epoxy Coatings Embedded by Modified Calcium Carbonate Particles
In this paper, electrochemical behavior of epoxy paints embedded by modified calcium carbonate particles was investigated during exposure to 3.5 wt% NaCl solution. The precipitated calcium carbonate (PCC) and ground calcium carbonate (GCC) particles were utilized as inexpensive filler for epoxy paints. Electrochemical impedance spectroscopy (EIS), polarization tests and pin-on-disk method w...
متن کامل