Characterization of electrical conductivity in a zeolitelike material
نویسندگان
چکیده
We present the electrical characterization of a zeolitelike oxo-vanadium arsenate framework. The experimentally obtained electronic and ionic conductivities and their interactions are discussed. Further, we investigate the potential use of electrically conducting zeolitelike materials in electrical energy storage applications, in light of the material’s structural and electronic characteristics. © 2009 American Institute of Physics. doi:10.1063/1.3251070
منابع مشابه
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملAn Insight into Colloidal Gas Aphron Drainage Using Electrical Conductivity Measurement
In the present paper Electrical Conductivity (EC) of Colloidal Gas Aphron (CGA) suspensions was measured for anionic and cationic surfactants (Sodium Dodecyl Sulfate (SDS) and Tetradecyl Trimethyl Ammonium Bromide (TTAB)). Experiments were made for different concentrations of SDS (6, 8.1, 10 mM) and TTAB (2, 3.51, 5 mM). CGA drainage behavior was observed and measured using 1 liter measuri...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملCharacterization Study for Nanocompositions of Methylene Blue and Riboflavin-Nafion on the Electrode Surface
Nafion is a perfluorinated anionic polyelectrolyte. The increasing popularity of nafion for the fabrication of redox polymer modified electrodes in recent years arises from easy fabrication, good electrical conductivity and high partition coefficients of many redox compounds in nafion. To investigate the production of nano-compositions by mixing electron transfer material and nafion polyme...
متن کاملSynthesis and Characterization of a Novel Nanoporous Composite Based on Elemental Sulfur and Graphitic Mesoporous Carbon
A novel sulfur nanocomposite was fabricated based on graphitic mesoporous carbon.The graphitic mesoporous carbon was synthesized using sucrose as carbon precursor, nano CaCO3 as a hard template and nickel nitrate as graphitization catalyst. The structural properties of the prepared material were characterized using powder X-Ray Diffraction (XRD), N2-adsorption/de...
متن کامل