The Effect of PVP Addition on the Mechanical Properties of [84%LLDPE: 15 %(( 100-X) %PP: X%PVP): 1%Basalt Particle] Polymer Blend Composites
ثبت نشده
چکیده
Polymer blends composites were prepared according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with weight ratios selected for X values (0,4,8,12,16 %), as strips by double screw extruder and use press process the strips to prepare the samples according ASTM specification, the mechanical properties were studied for all theprepared samples which are (tensile, flexural, compression, impact, hardness, and creep tests). The results are as following:results showed increment of mechanical properties as PVP ratio increases except elongation, furthermore the results recorded highest values of fracture strength, young modulus, compressive strength, flexural strength, maximum shear stress, flexural modulus and creep modulus at PVP 8% wt. which are (31.32MPa, 0.14GPa, 27.4MPa,24MPa, 0.6MPa, 1.08GPa and 0.558GPa) respectively. While the highest values of fracture toughness and hardness recorded at 12% wt. (1.4696Pa√m), and at 4% wt. (56.5) respectively.
منابع مشابه
Effect of Fe3+–MMT on thermal degradation and mechanical behavior of PVP/Amylose nanocomposite films
Novel nanocomposite films based on amylose (AM) and Fe3+-montmorillonite (Fe3+–MMT) in the matrix of poly (vinyl pyrrolidone) (PVP) were fabricated by using a solution casting method. The X-Ray diffractional analysis indicated that an ion-exchange process occurred between Fe3+–MMT and PVP. Thermogravimetrical analysis (TGA), differential termogravivetrical analy...
متن کاملThe Effect of Polyvinylpyrrolidone on the Formation of Copper Nanoplates in Wet-Chemical Reduction Method
In this work, we report synthesis and characterization of copper nanoparticles in polymer matrix by wet-chemical reduction method using ascorbic acid as reducing agent, copper (II) sulfate as metal precursor and polyvinylpyrrolidone k-30 (PVP K-30) as surfactant agent. The reaction was carried out in a high-speed stirring mixture at room temperature under nitrogen atmosphere. Characterization o...
متن کاملImprovement of Physico-mechanical Properties of Partially Amorphous Acetaminophen Developed from Hydroalcoholic Solution Using Spray Drying Technique
Objective(s): This study was performed aiming to investigate the effect of particle engineering via spray drying of hydroalcoholic solution on solid states and physico-mechanical properties of acetaminophen. Materials and Methods: Spray drying of hydroalcoholic solution (25% v/v ethanol/water) of acetaminophen (5% w/v) in the presence of small amounts of polyninylpyrrolidone K30 (PVP) (0, 1...
متن کاملThe Effect of Polyvinylpyrrolidone on the Formation of Copper Nanoplates in Wet-Chemical Reduction Method
In this work, we report synthesis and characterization of copper nanoparticles in polymer matrix by wet-chemical reduction method using ascorbic acid as reducing agent, copper (II) sulfate as metal precursor and polyvinylpyrrolidone k-30 (PVP K-30) as surfactant agent. The reaction was carried out in a high-speed stirring mixture at room temperature under nitrogen atmosphere. Characterization o...
متن کاملMechanical, Rheological and Computational Study of PVP/PANI with Additives
Polyvinylpyrrolidone/polyaniline emeraldine salt (PVP/PANI) with additives (TiO2, ZnO, NaCl, and Na2SO4) was synthesized via oxidative in situ polymerization. Because of using PVP/PANI as a protective membrane layer and its applications in an electrical device, we investigated the mechanical and rheological properties of PVP/PANI and other composites in orde...
متن کامل