Loading rates and the dynamic initiation toughness in brittle solids
نویسندگان
چکیده
The experimentally determined marked rise of the stress intensity factor required to initiate crack propagation in brittle solids under variably high loading rates, is analyzed. This problem of fracture initiation at the tip of a crack is considered in terms of activating a flaw at some distance away from the tip. By using a semi-infinite crack in an unbounded two-dimensional solid subjected to spatially uniform but temporally varying crack-face pressure, we consider the evolution of stress at the failure initiation site. Fracture initiation is assumed synonymous with attaining a critical stress at the fracture site. The results conform to typical experimental data of dynamic crack initiation in brittle solids.
منابع مشابه
Dynamic Initiation and Propagation of Multiple Cracks in Brittle Materials
Brittle materials such as rock and ceramic usually exhibit apparent increases of strength and toughness when subjected to dynamic loading. The reasons for this phenomenon are not yet well understood, although a number of hypotheses have been proposed. Based on dynamic fracture mechanics, the present work offers an alternate insight into the dynamic behaviors of brittle materials. Firstly, a sin...
متن کاملEffects of age and loading rate on equine cortical bone failure.
Although clinical bone fractures occur predominantly under impact loading (as occurs during sporting accidents, falls, high-speed impacts or other catastrophic events), experimentally validated studies on the dynamic fracture behavior of bone, at the loading rates associated with such events, remain limited. In this study, a series of tests were performed on femoral specimens obtained post-mort...
متن کاملDynamic fracture initiation in brittle materials under combined mode I/II loading
A new test method has been developed to measure the resistance of dynamic fracture initiation in brittle materials under combined mode I/I loadings. The Brazilian disks with center-cracks have been fractured under oblique impact loadings in diarnetral-compression. The dynamic stress intensity factors of mode I and H are evaluated from the superposition integrals of the step response functions f...
متن کاملA universal relation for edge chipping from sharp contacts in brittle materials: A simple means of toughness evaluation
An analysis of chipping fracture in brittle solids is presented. Cracks are introduced into the edges of selected materials, including soda-lime glass and fine-grain ceramics, using a Vickers indenter in monotonic loading. The ensuing chip morphology is examined and shown to exhibit a certain geometrical similarity, independent of material properties. A simple universal relation is derived for ...
متن کاملDynamic fragmentation of a brittle plate under biaxial loading: strength or toughness controlled?
The fragmentation of a brittle plate subjected to dynamic biaxial loading is investigated via numerical simulations. The aim is to extend our understanding of the dynamic processes affecting fragment size distributions. A scalable computational framework based on a hybrid cohesive zone model description of fracture and a discontinuous Galerkin formulation is employed. This enables large-scale s...
متن کامل