Thermal Equations of State of the α−, β−, and ω− Phases of Zirconium
نویسندگان
چکیده
Introduction Zirconium is a fascinating d-orbital transition metal. It has been widely used for nuclear and chemical applications owing to its low neutron absorption cross-section and its exceptional resistance to corrosion. The study of the fundamental thermodynamic properties of zirconium, such as equation of state (EOS) and phase stability, are very important for a better understanding of its crystal, chemical, and physical properties and to the development of theoretical modeling in computational physics [1,2].
منابع مشابه
Investigation of process factors in the synthesis of Ca7ZrAl6O18 cement by solid state method in order to eliminate undesirable secondary phases
One of the widely used cements for filling teeth and bones can be calcium zirconium aluminate cement Ca7ZrAl6O18, which of course can also be used as a refractory. The behavior and properties of this cement are more similar to tricalcium aluminate C3A cement. In this study, C7A3Z cement was synthesized by using commercial calcium carbonate, alumina and zirconia powders and after grinding for 4-...
متن کاملIs the Freeze Drying Method Effect on the Phase Transition Temperature ofβ/β́́ Lithium Zirconium Phosphate?
Spherical granules of the superionic conductor β/β́ LiZr2(PO4)3 in the range of sub 100 nm sizewere synthesizedvia freeze drying methodand fully reviewed in all aspects. Samples were characterized by the X-ray diffractometry (XRD), the Thermal analysis (TG, DSC), theFourier Transform Infra-Red Spectroscopy (FTIR) and the Scanning Electron Microscopy (SEM).Their structuredepends largely on the me...
متن کاملEffects of time, temperature and precursor on solid state synthesis of α-TCP
The effects of solid state synthesis process parameters (time and temperature) and primary calcium precursor on the amount of produced α-tricalcium phosphate (Ca3(PO4)2 or α -TCP) have been investigated. α-TCP was synthesized by firing of stoichiometric amount of calcium carbonate and monetite in first group and calcium carbonate and brushite in the second group, once at 1350°C for 3,6,8,16 h d...
متن کاملA Comparative Study of the Synthesis and Thermal Stability of Nanostrucrured Al and Al-Mg Powders Fabricated by Mechanical Alloying Technique
Nanostructured Al and Al-Mg (Mg 30 wt. %) powders with the mean crystallite sizes of 42 and 11 nm were prepared through the solid state ball milling technique. The milling process was performed for various times up to 12 h in argon atmosphere and the synthesized powders were in detail characterized by different techniques. The effect of milling time and Mg addition on the size, morphology, chem...
متن کاملSynthesizing and Characterization of Monoclinic and Tetragonal Phases of Zirconium Oxide (Zro2) Nanofibers with the Aid of Electrospinning Technique
Zirconium oxide has found extensive applications in various industries becauseof its excellent properties such as high strength; high-temperature resistance;extraordinary wearing resistance; ionic conductivity; and corrosion resistance. Also, someProperties like high melting point, high mechanical and thermal strength, high dielectricconstant and low conductivity have in...
متن کامل