Effect of solution treatment on the fatigue behavior of an as-forged Mg-Zn-Y-Zr alloy
نویسندگان
چکیده
Through investigating and comparing the fatigue behavior of an as-forged Mg-6.7Zn-1.3Y-0.6Zr (wt.%) alloy before and after solid solution treatment (T4) in laboratory air, the effect of T4 treatment on fatigue crack initiation was disclosed. S-N curves illustrated that the fatigue strength of as-forged samples was 110 MPa, whereas the fatigue strength of T4 samples was only 80 MPa. Observations to fracture surfaces demonstrated that for as-forged samples, fatigue crack initiation sites were covered with a layer of oxide film. However, due to the coarse grain structure and the dissolution of MgZn2 precipitates, the activation and accumulation of {10-12} twins in T4 samples were much easier, resulting in the preferential fatigue crack initiation at cracked twin boundaries (TBs). Surface characterization demonstrated that TB cracking was mainly ascribed to the incompatible plastic deformation in the twinned area and nearby α-Mg matrix.
منابع مشابه
Effect of solution treatment on stress corrosion cracking behavior of an as-forged Mg-Zn-Y-Zr alloy
Effect of solid solution treatment (T4) on stress corrosion cracking (SCC) behavior of an as-forged Mg-6.7%Zn-1.3%Y-0.6%Zr (in wt.%) alloy has been investigated using slow strain rate tensile (SSRT) testing in 3.5 wt.% NaCl solution. The results demonstrated that the SCC susceptibility index (ISCC) of as-forged samples was 0.95 and its elongation-to-failure (εf) was only 1.1%. After T4 treatmen...
متن کاملBiodegradable Mg-Zn-Y alloys with long-period stacking ordered structure: optimization for mechanical properties.
To optimize the mechanical properties for biodegradable orthopedic implant, microstructures and tensile properties of Mg-Zn-Y alloys containing long period stacking ordered (LPSO) phase were investigated. For the as-cast Mg(100-3x)(Zn(1)Y(2))(x) (1 ≤ x ≤ 3) alloys, volume fraction of 18R LPSO phase increases with increasing the contents of Zn and Y. Mg(97)Zn(1)Y(2) alloy exhibits the optimal co...
متن کاملFabrication of the Cu-Zn multilayer and Cu-Zn alloy by accumulative roll bonding (ARB) with an emphasis on the wear behavior
Accumulative roll bonding (ARB) was used to fabricate the Cu-Zn multilayer and Cu-Zn solid solution. A lamellar structure with the hardness of about 130 VHN was formed after eight ARB cycles. Following to the suitable heat treatment, a solid solution with a uniform microstructure and hardness of about 57 VHN was produced. The dominant wear mechanism in the ARB processed multilayer was found to ...
متن کاملIn vitro degradation behavior and cytocompatibility of Mg–Zn–Zr alloys
Zinc and zirconium were selected as the alloying elements in biodegradable magnesium alloys, considering their strengthening effect and good biocompatibility. The degradation rate, hydrogen evolution, ion release, surface layer and in vitro cytotoxicity of two Mg-Zn-Zr alloys, i.e. ZK30 and ZK60, and a WE-type alloy (Mg-Y-RE-Zr) were investigated by means of long-term static immersion testing i...
متن کاملEffect of Be, Zr and Heat Treatment on Mechanical Behavior of Cast Al-Mg-Zn-Cu Alloys (7075)
The present study was undertaken to investigate the effect of aging parameters (time and temperature) on the mechanical properties of Be-and/or Zrtreated Al-Mg-Zn (7075) alloys. Ultimate tensile strength, 0.5% offset yield strength and % elongation measurements were carried out on specimens prepared from cast and heat treated 7075 alloys containing Be and/or Zr. Different aging treatment were c...
متن کامل