Failure of the cement-bone interface.
نویسنده
چکیده
We report the early failure, at a mean of 37 months, of 17 femoral prostheses due to aseptic loosening at the cement-bone interface. In every case the prosthesis had been manufactured with a surface coating designed to enhance the strength of the cement-prosthesis interface. It is postulated that improving the bond at the cement-prosthesis interface may transfer increased stress to the cement-bone interface and cause early failure at that interface.
منابع مشابه
Cement-Implant Interface Fracture Failure by Crack Initiation Due to Interface Cavity Stress Concentration
Nowadays total joint replacements are widely used in the world, so in average 800,000 joint surgeries are done yearly only in Europe and North America. However implant loosening is and remains as the major issue of all implant failures and therefore causes revision surgery procedures. Studies and experiments have identified poor fixation of implants most likely is the main cause of long term im...
متن کاملMechanical characteristics of the bone-graft-cement interface after impaction allografting.
Impaction allografting is an attractive procedure for the treatment of failed total hip replacements. The graft-cement-host bone interface after impaction allografting has not been characterized, although it is a potential site of subsidence for this type of revision total hip reconstruction. In six human cadaveric femurs, the cancellous bone was removed proximally and local diaphyseal lytic de...
متن کاملBone-cement interface of the glenoid component: stress analysis for varying cement thickness.
BACKGROUND Although shoulder arthroplasty is an accepted treatment for osteoarthritis, loosening of the glenoid component, which mainly occurs at the bone-cement interface, remains a major concern. Presently, the mechanical effect of the cement mantel thickness on the bone-cement interface is still unclear. METHODS Finite element analysis of a prosthetic scapula was used to evaluate the effec...
متن کاملPorosity reduction in bone cement at the cement-stem interface.
The fatigue failure of bone cement, leading to loosening of the stem, is likely to be one mode of failure of cemented total hip replacements. There is strong evidence that cracks in the cement are initiated at voids which act as stress risers, particularly at the cement-stem interface. The preferential formation of voids at this site results from shrinkage during polymerisation and the initiati...
متن کاملCement oscillation increases interlock strength at the cement-bone interface, with commentary.
Modern cementing techniques aim to improve the interlock between bone and cement and to establish a durable interface. Cement penetration is generally believed to influence interface failure, but current methods for improving the cement-bone interface are inadequate. Oscillation is the reciprocated movement of an object through its balanced position, or the quantum physics of systematic fluctua...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- The Journal of bone and joint surgery. British volume
دوره 77 1 شماره
صفحات -
تاریخ انتشار 1995