Synthesis and Evaluation of Calcium-Deficient Hydroxyapatite with SiO2
نویسندگان
چکیده
Effect of SiO2 addition on the microstructures of calcium-deficient hydroxyapatite prepared by the heat-treatments was examined. Obtained hydroxyapatites substituted with Si ion were characterized by XRD, FT-IR and XAFS measurements. XANES results of Si K-edge and P K-edge in these modified hydroxyapatites indicated the shift of peaks of P K-edge with the SiO2 contents, although no change of Si local structures. In this study, the effect of Si ion on microand local structure of hydroxyapatite with SiO2 addition was mainly clarified.
منابع مشابه
Sol-gel synthesis of FHA / CDHA nanoparticles with a nonstochiometric ratio
The aim of this study was to investigate the sol gel synthesis of HA/FA nanoparticles and the possible formation of TCP phase or unstoichiometric calcium deficient hydroxyapatite (CDHA) from the precursors with a Ca/P ratio of 1.62. In order to prepare the sol, the solutions of Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol were used respectively as P, F and Ca precursors....
متن کاملSol-gel synthesis of FHA / CDHA nanoparticles with a nonstochiometric ratio
The aim of this study was to investigate the sol gel synthesis of HA/FA nanoparticles and the possible formation of TCP phase or unstoichiometric calcium deficient hydroxyapatite (CDHA) from the precursors with a Ca/P ratio of 1.62. In order to prepare the sol, the solutions of Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol were used respectively as P, F and Ca precursors....
متن کاملThe Effect of Rotation Speed and Time of Milling on Synthesis and Properties of Fluoridated Hydroxyapatite Biomaterial
Synthetic hydroxyapatite (HA) is the most helpful because of its similarity to natural bone in both crystalline structure and chemical composition. Recently, fluoridated hydroxyapatite (FHA) has been developed in dental and orthopedic application because it has lower solubility than pure HA, while maintaining the comparable bioactivity and biocompatibility. The aim of this study was to...
متن کاملSynthesis and Characterization of Hydroxyapatite Nanocrystals via Chemical Precipitation Technique
In this study, hydroxyapatite (HA) nanocrystals have been synthesized via chemical precipitation technique. Diammonium hydrogen phosphate and calcium nitrate 4-hydrate were used as starting materials and sodium hydroxide solution was used as the agent for pH adjustment. The powder sample was evaluated by techniques such as scanning electron microscope, transmission electron microscope, Fou...
متن کاملSynthesis, characterization and biocompatibility evaluation of hydroxyapatite - gelatin polyLactic acid ternary nanocomposite
Objective(s): The current study reports the production and biocompatibility evaluation of a ternary nanocomposite consisting of HA, PLA, and gelatin for biomedical application.Materials and Methods: Hydroxyapatite nanopowder (HA: Ca10(PO4)6(OH)2) was produced by burning the bovine cortical bone within the temperature range of 350-450 oC followed by heating in an oven at 800. Synthesis of the te...
متن کامل