Waste derived glass ceramic composites prepared by low temperature sintering/sinter-crystallisation
نویسندگان
چکیده
Waste derived glass ceramic composites prepared by low temperature sintering/sinter-crystallisation I. Ponsot, R. Detsch, A. R. Boccaccini & E. Bernardo To cite this article: I. Ponsot, R. Detsch, A. R. Boccaccini & E. Bernardo (2015) Waste derived glass ceramic composites prepared by low temperature sintering/sinter-crystallisation, Advances in Applied Ceramics, 114:sup1, S17-S25, DOI: 10.1179/1743676115Y.0000000044 To link to this article: http://dx.doi.org/10.1179/1743676115Y.0000000044
منابع مشابه
Vitrification and Sinter-Crystallization of Iron-Rich Industrial Wastes
Results about the vitrification of several hazardous iron-rich industrial wastes (from productions of Zn and Cu metals, as well as EAFD and MSWA) and the usage of obtained glasses for synthesise of sintered glass-ceramics are summarises. It is shown that the appropriated method of sinter-crystallization mainly depends on the crystallization trend of used glasses. When the parent composition is ...
متن کاملSinter-crystallisation in the diopside–albite system Part I. Formation of induced crystallisation porosity
The sinter-crystallisation was investigated in three model glasses (G1, G2 and G3) belonging to the diopside–albite system and forming between 30 and 60% diopside, respectively. The effect of bulk crystallisation on the sintering was studied by the addition of 0.7 wt.% Cr2O3 as nucleating agent to the G2 glass. The degree of sintering was evaluated by the variation of the apparent density while...
متن کاملCompressibility and Foaming behavior of steel slag/waste glass compositesby particle size distribution and foam agents
In present research, the foam glass-ceramic composites fabricated by window glass, steel slag and SiC, CaCO3 foaming agents were investigated by press–sintering method. The optimum sintering temperature was obtained at 1200°C with a 3-minutes holding time and 20°C/min heating rate. The optimum pressure level of 80 MPa for achieving the 70 % of relative density was selected. The effec...
متن کاملPreparation and Analysis of MBS based Glass-Ceramic for LTCC Applications
In this paper the MBS (Magnesium borosilicate) based glass-ceramic have been prepared and characterised to find its suitability in Low temperature cofired ceramics (LTCC) technology. The glass-ceramics were prepared by using conventional solid state route. The experimental study was conducted on the MBS glass-ceramic containing MAS (Magnesium Alumino-Silicate) based glass-ceramic as an additive...
متن کاملSinter-crystallization in the diopside–albite system Part II. Kinetics of crystallization and sintering
The formation of intragranular pores, induced by diopside crystallization in diopside–albite glasses, was highlighted in a previous study and here confirmed by SEM observation. The sinter-crystallization kinetics of four glass compositions, labelled G1, G2, G3 and G2-Cr, characterized by the formation of induced crystallisation porosity, PCR, was investigated. The activation energies of crystal...