Characterization of Human Gingival Fibroblasts on Zirconia Surfaces Containing Niobium Oxide
نویسندگان
چکیده
It was indicated that tetragonal zirconia polycrystal (TZP) containing yttria (Y₂O₃) and niobium oxide (Nb₂O₅) ((Y,Nb)-TZP) could be an adequate dental material to be used at esthetically important sites. The (Y,Nb)-TZP was also proved to possess its osteogenic potential comparable with those conventional dental implant material, titanium (Ti). The objective of the current study was to characterize cellular response of human gingival fibroblasts (HGFs) to smooth and rough surfaces of the (Y,Nb)-TZP disc, which were obtained by polishing and sandblasting, respectively. Various microscopic, biochemical, and molecular techniques were used to investigate the disc surfaces and cellular responses for the experimental (Y,Nb)-TZP and the comparing Ti groups. Sandblasted rough (Y,Nb)-TZP (Zir-R) discs had the highest surface roughness. HGFs cultured on polished (Y,Nb)-TZP (Zir) showed a rounded cell morphology and light spreading at 6 h after seeding and its proliferation rate significantly increased during seven days of culture compared to other surfaces. The mRNA expressions of type I collagen, integrin α2 and β1 were significantly stimulated for the Zir group at 24 h after seeding. The current findings, combined with the previous results, indicate that (Y,Nb)-TZP provides appropriate surface condition for osseointegration at the fixture level and for peri-implant mucosal sealing at the abutment level producing a suitable candidate for dental implantation with an expected favorable clinical outcome.
منابع مشابه
Dicationic Imidazolium-Based Ionic Liquid Coatings on Zirconia Surfaces: Physico-Chemical and Biological Characterization
In the present work, dicationic imidazolium-based ionic liquids (ILs) were investigated as multi-functional coatings on a zirconia (ZrO₂) surface to prevent biofilm formation and enhance the wear performance of zirconia while maintaining the material's compatibility with host cells. ILs containing phenylalanine and methionine were synthesized and deposited on zirconia. Intermolecular interactio...
متن کاملComparison of the Osteogenic Potential of Titanium and Modified Zirconia-Based Bioceramics
Zirconia is now favored over titanium for use in dental implant materials because of its superior aesthetic qualities. However, zirconia is susceptible to degradation at lower temperatures. In order to address this issue, we have developed modified zirconia implants that contain tantalum oxide or niobium oxide. Cells attached as efficiently to the zirconia implants as to titanium-based material...
متن کاملModulation of human dermal microvascular endothelial cell and human gingival fibroblast behavior by micropatterned silica coating surfaces for zirconia dental implant applications
Dental ceramic implants have shown superior esthetic behavior and the absence of induced allergic disorders when compared to titanium implants. Zirconia may become a potential candidate to be used as an alternative to titanium dental implants if surface modifications are introduced. In this work, bioactive micropatterned silica coatings were produced on zirconia substrates, using a combined met...
متن کاملEffect of Clinically Relevant CAD/CAM Zirconia Polishing on Gingival Fibroblast Proliferation and Focal Adhesions
Mucosal seal formation around dental abutments is critical to the successful integration of dental implants into the human oral cavity. No information exists for how clinically relevant polishing procedures for computer-aided design and computer-aided manufactured (CAD/CAM) zirconia abutments affects cellular responses important to mucosal seal formation. CAD/CAM zirconia was divided into four ...
متن کاملAdhesion and Proliferation of Human Gingival Fibroblasts on Root Surfaces following Photodynamic Therapy: An In Vitro Study
Background and Aim: Previous studies have shown that some dyes used in photodynamic therapy (PDT) have a low pH and may cause root demineralization and remove the smear layer. This study aimed to assess and compare the effects of root biomodification with citric acid and PDT on the adhesion and proliferation of human gingival fibroblasts (HGFs). Materials and Methods: In this in vitro experime...
متن کامل