Magnetic hardening of Zr2Co11:(Ti, Si) nanomaterials
نویسندگان
چکیده
The role of Ti and Si additions in the magnetic hardening of rapidly quenched Zr2Co11-based nanomaterials has been investigated. Nanocrystalline Zr17–xTixCo83 and Zr18Co82–ySiy are mainly composed of rhombohedral Zr2Co11 and a small amount of orthorhombic Zr2Co11, hcp Co, and cubic Zr6Co23. Ti addition decreases the mean grain size of the magnetic phases, and thus increases coercivity and energy product from 1.6 kOe and 1.9 MGOe for x = 0 to 2.6 kOe and 3.9 MGOe for x = 2, respectively. Si addition enhances the anisotropy field of the hard phase which increases the coercivity but slightly decreases the magnetization. This work shows that Ti has a positive effect on energy product through refinement of structure.
منابع مشابه
Effect of annealing on nanostructure and magnetic properties of Zr2Co11 material
Single-phase Zr2Co11 nanomagnetic materials with high coercivity have been fabricated by melt spinning with subsequent annealing under Ar, N2, and vacuum. Annealing coarsens the grains and decreases the density of defects, leading to intergrain decoupling action and the enhancement of the magnetocrystalline anisotropy field of the hard magnetic phase. Therefore, coercivity increases 44.7% from ...
متن کاملPhotoelectrochemical Water Splitting Properties of Ti-Ni-Si-O Nanostructures on Ti-Ni-Si Alloy
Ti-Ni-Si-O nanostructures were successfully prepared on Ti-1Ni-5Si alloy foils via electrochemical anodization in ethylene glycol/glycerol solutions containing a small amount of water. The Ti-Ni-Si-O nanostructures were characterized by field-emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and diffuse reflectance absorption spectra....
متن کاملHigh Refractive Organic–Inorganic Hybrid Films Prepared by Low Water Sol-Gel and UV-Irradiation Processes
Organic-inorganic hybrid sols (Ti-O-Si precursor) were first synthesized by the sol-gel method at low addition of water, and were then employed to prepare a highly refractive hybrid optical film. This film was obtained by blending the Ti-O-Si precursor with 2-phenylphenoxyethyl acrylate (OPPEA) to perform photo-polymerization by ultraviolet (UV) irradiation. Results show that the film transpare...
متن کاملRole of Metal Lattice Expansion and Molecular π-Conjugation for the Magnetic Hardening at Cu–Organics Interfaces
Magnetic hardening and generation of room-temperature ferromagnetism at the interface between originally nonmagnetic transition metals and π-conjugated organics is understood to be promoted by interplay between interfacial charge transfer and relaxation-induced distortion of the metal lattice. The relative importance of the two contributions for magnetic hardening of the metal remains unquantif...
متن کاملThe Effect of Inversion Time on the Relationship Between Iron Oxide Nanoparticles Concentration and Signal Intensity in T1-Weighted MR Images
BACKGROUND Magnetic nanoparticles have been widely applied in recent years for biomedical applications. Signal intensity (SI) of magnetic resonance (MR) images depends on the concentration of nanoparticles. It is important to find the minimum concentration of iron oxide nanoparticles that produces maximum SI and determines the minimum injection dose for clinical studies. OBJECTIVES This study...
متن کامل