Gas nitriding and subsequent oxidation of Ti-6Al-4V alloys
نویسندگان
چکیده
Ti-6Al-4V alloys consisting of α-Ti grains and intergranular β-Ti islands were nitrided at 850°C for 1 to 12 h under a nitrogen pressure of 1 Pa. With increasing nitriding time, the Ti-N compound layer became thicker, and the α-Ti diffusion zone containing dissolved nitrogen became wider. In the Ti-N compound layer, the initially formed Ti2N became TiN as the nitriding progressed. The nitride layers were oxidized to rutile-TiO2 after oxidation at 700°C for 10 h in air.
منابع مشابه
Investigation of the mechanical properties and microstructure of the Ti-6Al-4V to Al2024 joint fabricated by successive- stage transient liquid phase (S-TLP) method
The aim of this study is investigation of TLP variables on microstructure and mechanical properties of Al2024 to Ti-6Al-4V bonding for TLP joint. For this purpose, the sheets were prepared with dimension of 130×32×3 mm from Ti-6Al-4V and Al2024 alloys and 50µm thick Sn-5.3Ag-4.2Bi foil as interlayer. Sn-5.3Ag-4.2Bi foil prepared with dimension of 32×25 mm. Two alloys was joint together by proce...
متن کاملInvestigation of the mechanical properties and microstructure of the Ti-6Al-4V to Al2024 joint fabricated by successive- stage transient liquid phase (S-TLP) method
The aim of this study is investigation of TLP variables on microstructure and mechanical properties of Al2024 to Ti-6Al-4V bonding for TLP joint. For this purpose, the sheets were prepared with dimension of 130×32×3 mm from Ti-6Al-4V and Al2024 alloys and 50µm thick Sn-5.3Ag-4.2Bi foil as interlayer. Sn-5.3Ag-4.2Bi foil prepared with dimension of 32×25 mm. Two alloys was joint together by proce...
متن کاملA survey of surface treatments to improve the fretting fatigue resistance of Ti-6Al-4V
The effects of surface modification treatments such as shot peening, ion implantation (carbon and nitrogen), surface lubrication (soft coating), laser gas nitriding and various combinations thereof, on the fretting fatigue resistance of Ti-6Al-4V have been investigated. The best of these surface treatments appears to be shot peening. While ion implantation improves the base metal fretting fatig...
متن کاملEffect of Gas-Diffusion Oxynitriding on Microstructure and Hardness of Ti-6Al-4V Alloys
The commercially available titanium alloy, Ti-6Al-4V, was oxynitrided in the deoxygenated nitrogen gas at high temperatures followed by cooling in oxygen-containing nitrogen in order to analyze the influence of oxynitriding parameters on the phase modification, hardness, and the microstructural evolution of the oxynitrided coating. The surface microhardness of the oxynitrided alloy increased du...
متن کاملAn investigation on metallurgical and mechanical properties of vacuum brazed Ti-6Al-4V to 316L stainless steel using Zr-based filler metal
Both Ti-6Al-4V and 316L stainless steels are widely used as engineering alloys. Fusion welding of these two alloys is not easily possible due to their incomplete solubility in each other. Brazing is one of the best choices for joining dissimilar alloys. In this study, wettability experiments were done at 940 and 970 ºC for 5, 15 and 30 min. Also, joining of these two alloys was carried out at 9...
متن کامل