Nanoscale Strain Fields Research of Boundaries between B2 Matrix and G.P. Zone in Ni-Ti Alloy Thin Films
نویسندگان
چکیده
Ti-47 at.%Ni alloy films were prepared by magnetron sputtering followed by 460°C for 40 minutes heat-treatment. The strain fields between B2 phase matrix and G.P. zone were mapped by a combination of high-resolution transmission electron microscopy and geometric phase analysis method. It was found that there is a compressive strain region parallel to the longitudinal axis of G.P. zone with 2 nm in width, -2.2% in average strain at the boundaries between B2 phase and G.P. zone.
منابع مشابه
Electron Microscopy Studies of Martensite Microstructures
An overview will be given of some recent results of microstructural electron microscopy studies on martensitic systems. The precursor structure observed in a ternary Ni-Mn-Ti alloy and its correlation with the ensuing stacking sequence is presented. New types of materials of a well known alloy, in casu splat-cooled and nanoscale thin films of Ni-A1 are investigated revealing particular morpholo...
متن کاملDependence of Nanostructure and the Optical Properties of Ni Thin Films with Different Thicknesses on the Substrate Temperature
Nickel films with the thicknesses of 30 and 120 nm were deposited on glass substrates, at different substrate temperatures (313 to 600 K) under uhv condition. The nano-structure of the films and mean diameter of grains was obtained for each films using atomic force microscopy (AFM). Their optical properties were measured by spectrophotometry in the spectral range of 190-2500 nm. Kramers-Kronig ...
متن کاملStructure of the secondary phase and its effects on hydrogen-storage properties in a Ti Zr V Ni alloy
The phase structures and hydrogen storage properties of a Ti Zr V Ni alloy are studied. It is found that this alloy consists of a 0.7 0.2 0.1 matrix and a secondary phase. The matrix is a B2-type compound with bcc structure and the secondary phase is a C14-type Laves phase with hexagonal structure. This alloy electrode has a larger charge–discharge capacity than stoichiometric TiNi electrodes b...
متن کاملEffects of Cu on the microstructural and mechanical properties of sputter deposited Ni-Ti thin films
The microstructure of sputter deposited Ti-rich Ni-Ti thin films doped with Cu in the range 020.4 at.% and annealed for 1 h at 500 and 600°C has been investigated and correlated with the mechanical properties of the films measured by depth-sensing nanoindentation. X-ray diffraction analysis showed the microstructural evolution of Ni-Ti thin films when doped with Cu and annealed at different tem...
متن کاملCorrosion of Ni-Ti Rotary Instruments: A Review
The nickel-titanium (Ni-Ti) alloys used in endodontics contain 56% Ni and 44% Ti. The 2 unique features related to clinical dentistry (i.e., shape memory effect and superelasticity) are due to the transition from austenite to martensite in Ni-Ti alloy. When a superelastic Ni-Ti alloy undergoes a low tensile loading, normal elastic behavior occurs. In fact, at higher tensile loads, the elastic s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
دوره 2014 شماره
صفحات -
تاریخ انتشار 2014