Preparation and Electrical Properties of Insulation Paper Composed of SiO2 Hollow Spheres
نویسندگان
چکیده
SiO2 hollow spheres and low relative permittivity insulation paper handsheets composed of these SiO2 hollow spheres with different weight percentages were successfully prepared. Low-content SiO2 hollow spheres were uniformly dispersed in the insulation paper handsheets. The relative permittivity of the immersed oil Kraft-SiO2 hollow sphere handsheets (K-SiO2) initially decreased and then increased with increased amount of SiO2 hollow spheres. K-5% SiO2 possessed the lowest relative permittivity of approximately 1.68 at 50 Hz. The breakdown voltage of the paper-oil-paper composite insulation system increased from 26.4 kV to 30.5 kV with decreased relative permittivity of the paper from 2.55 to 1.68. The relationship between the relative permittivity and electric field strength of typical samples were also calculated.
منابع مشابه
Preparation of Hollow CuO@SiO2 Spheres and Its Catalytic Performances for the NO + CO and CO Oxidation
The hollow CuO@SiO2 spheres with a mean diameter of 240 nm and a thin shell layer of about 30 nm in thickness was synthesized using an inorganic SiO2 shell coating on the surface of Cu@C composite that was prepared by a two-step hydrothermal method. The obtained hollow CuO@SiO2 spheres were characterized by ICP-AES, nitrogen adsorption-desorption, SEM, TEM, XRD, H2-TPR, CO-TPR, CO-TPD and NO-TP...
متن کاملPreparation and Characterization of Double Shell Fe3O4 Cluster@Nonporous SiO2@Mesoporous SiO2 Nanocomposite Spheres and Investigation of their In Vitro Biocompatibility
Background: Multifunctional core-shell magnetic nanocomposite particles with tunable characteristics have been paid much attention for biomedical applications in recent years. A rational design and suitable preparation method must be employed to be able to exploit attractive properties of magnetic nanocomposite particles. Objectives: Herein, we report on a simple approach for the synthesis of m...
متن کاملFabrication of TiO2 Hollow Spheres and its Application in Modification of Carbon Paste Electrode For Simultaneous Determination of Dopamine and Piroxicam in the Presence of Ascorbic acid
In this work we report preparation TiO2 hollow spheres and its application as an electrochemical sensor. Therefore the novel carbon paste electrode modified with TiO2 hollow spheres (TOHS), multi-walled carbon nanotubes (MWCNTs) and poly-glutamic acid (PGA) film (PGA/TOHS/MWCNTs/CPE) was used for simultaneous determination of dopamine (DA) and piroxicam (PRX) in the presence of ascorbic acid (A...
متن کاملPartial Discharge Characteristics of Polymer Nanocomposite Materials in Electrical Insulation: A Review of Sample Preparation Techniques, Analysis Methods, Potential Applications, and Future Trends
Polymer nanocomposites have recently been attracting attention among researchers in electrical insulating applications from energy storage to power delivery. However, partial discharge has always been a predecessor to major faults and problems in this field. In addition, there is a lot more to explore, as neither the partial discharge characteristic in nanocomposites nor their electrical proper...
متن کاملSonochemical preparation of hollow nanospheres and hollow nanocrystals.
Ceramic hollow spheres of MoS2 and MoO3 were obtained by sonochemical synthesis of MoS2 and MoO3 templated on silica nanoparticles (diameters 50-500 nm) followed by acid etching to remove the silica core. The resulting hollow materials have been characterized by elemental analysis, XPS, SEM, TEM, optical absorption, and hydrodesulfurization (HDS) studies. The TEM studies on the hollow ceramic m...
متن کامل