Formation of Alumina Nanocapsules by High-Energy-Electron Irradiation of Na-dawsonite Nanorods
نویسندگان
چکیده
We report the synthesis of unique Al2O3 nanocapsules by high-energy-electron irradiation of Na-dawsonite and a formation mechanism different from thermal decomposition which usually produces NaAlO2. The novel decomposition process may open up a shortcut for fabricating hollow nanostructures.
منابع مشابه
Microwave-assisted rapid synthesis of Co3O4 nanorods from CoC2O4.2H2O nanorods and its application in photocatalytic degradation of methylene blue under visible light irradiation
In this work, Co3O4 nanorods were successfully prepared by microwave-assisted solid state decomposition of rod-like CoC2O4.2H2O precursor within a very short reaction time (6 min) without the use of a solvent/surfactant and complicated equipment. The as-obtained Co3O4 nanorods were fully characterized by X-ray diffract...
متن کاملMicrowave-assisted rapid synthesis of Co3O4 nanorods from CoC2O4.2H2O nanorods and its application in photocatalytic degradation of methylene blue under visible light irradiation
In this work, Co3O4 nanorods were successfully prepared by microwave-assisted solid state decomposition of rod-like CoC2O4.2H2O precursor within a very short reaction time (6 min) without the use of a solvent/surfactant and complicated equipment. The as-obtained Co3O4 nanorods were fully characterized by X-ray diffract...
متن کاملFabrication and nanostructural characterization of TiO2 nanorods
TiO2 nanorods are synthesized by a thermal corrosion. In present work, synthesis of TiO2 nanorods in anatase, rutile and Ti8O15 phases, by using the sol-gel method and alkaline corrosion are reported. The morphologies and crystal structures of TiO2 nanorods are characterized by use of field emission scanning electron microscopy, atomic force microscopy and X-ray diffractometer techniques. The o...
متن کاملSonochemical fabrication and characterization of stibnite nanorods.
Regular stibnite (Sb(2)S(3)) nanorods with diameters of 20-40 nm and lengths of 220-350 nm have been successfully synthesized by a sonochemical method under ambient air from an ethanolic solution containing antimony trichloride and thioacetamide. The as-prepared Sb(2)S(3) nanorods are characterized by employing techniques including X-ray powder diffraction, X-ray photoelectron spectroscopy, sca...
متن کاملHydrothermal Synthesis of Aligned Hydroxyapatite Nanorods with Ultra-High Crystallinity
Hydroxyapatite nanorods aligned with ultrahigh crystallinity and high-yield were successfully synthesized through a hydrothermal approach. In this experiment, a new composition of cetyltrimethylammonium bromide ((CH3(CH2)15N+(CH3)3Br-) was designated as CTAP)/Ca(NO3)2/(NH4)2HPO4/NaOH and distilled water under hydrothermal condition, to synthesize single crystalHAp nanorods with diameter of 20 ±...
متن کامل