Influence of lack-of-fusion defects on load capacity of MAG welded joints
نویسندگان
چکیده
Pressure vessels operating at elevated temperatures and pressures are made of creep resisting plate and welded from individual components using the MAG welding process. The paper proposed focuses on the occurrence of lack-of-fusion defects in MAG welded plate components of pressure vessels. Lack of fusion, which is a planar defect and is, therefore, difficult to detect by common NDT methods, can result in catastrophic consequences since the latter do not only damage a pressure vessel but also jeopardize the environment and workers' health. The present paper deals with a research on the influence of a welding speed in welding of plate components made of S235JR steel of 8 mm in thickness, special care being taken to deliberately produce lack-of-fusion defects and possibly other weld defects. Test pieces prepared so as to contain various lack-of-fusion defects were subjected to destructive tensile testing. The force required for a weld failure was compared to actual weld defects. In the test pieces produced with lower welding speeds, a failure occurred in the welded joint and along a lack-of-fusion defect. In the test pieces produced with higher welding speeds, however, a fracture occurred outside a weld, although lack of fusion was present in the weld. Parallel to the tensile tests, radiographic examinations of lack-of-fusion defects were conducted and relevant micro sections were analysed. The aim of the study conducted was to elaborate a guideline for quality welding of plate components of pressure vessels.
منابع مشابه
Vulnerability Assessment of Steel Structures in District 12 of Mashhad City and Prioritizing the Welding Defects Using the Analytic Hierarchy Process
Recently, steel structures have been accounted for a large percentage of the buildings due to their advantages such as higher execution speed and easier construction. In steel structures, welded joints are commonly used and their quality plays a key role in stability of buildings under applied loads. Hence, to increase resiliency of welded steel structures against natural hazards, welded joints...
متن کاملResistance spot welding of AISI 201 stainless steel: The relationship between welding current, microstructure, mechanical properties and failure mode
In this paper, resistance spot welding process of AISI 201 stainless steel is studied experimentally. For this purpose, effect of welding current on quality of weld is investigated and relationships between welding current and fusion zone characteristics are examined. For determining mechanical properties such as maximum load and fracture mode, tensile - shear test of spot welds is performed. ...
متن کاملResistance spot welding of AISI 201 stainless steel: The relationship between welding current, microstructure, mechanical properties and failure mode
In this paper, resistance spot welding process of AISI 201 stainless steel is studied experimentally. For this purpose, effect of welding current on quality of weld is investigated and relationships between welding current and fusion zone characteristics are examined. For determining mechanical properties such as maximum load and fracture mode, tensile - shear test of spot welds is performed. ...
متن کاملX-Ray Radiography of EB Welded Joints in India
Electron Beam welding is becoming more important in Indian industries due to the growing automation of the process and superior weld quality, resulting from virtually zero heat affected zone (HAZ). Two main types of defects are often encountered in EB welding joints viz void type defects and crack type. EB welding joints must be radiographically inspected for all these types of defects and it i...
متن کاملStress Intensity Factor Expression for Welded Butt Joint with Undercut and Inclined Lack of Penetration Defects considering the Effect of Joint Shape
In this paper, the stress intensity factor (SIF) expression for defected butt welds containing undercut and inclined lack of penetration (LOP) subject to far-field tensile stress is derived. Some of the standards such as ISO 5817 and BS EN 25817 have specified allowable limits for the length of the undercut and LOP defects and for the height of the weld. In addition, EN 29692 standard has deter...
متن کامل