The Effect of Zeolite Composition and Grain Size on Gas Sensing Properties of SnO2/Zeolite Sensor
نویسندگان
چکیده
In order to improve the sensing properties of tin dioxide gas sensor, four kinds of different SiO₂/Al₂O₃ ratio, different particle size of MFI type zeolites (ZSM-5) were coated on the SnO₂ to prepared zeolite modified gas sensors, and the gas sensing properties were tested. The measurement results showed that the response values of ZSM-5 zeolite (SiO₂/Al₂O₃ = 70, grain size 300 nm) coated SnO₂ gas sensors to formaldehyde vapor were increased, and the response to acetone decreased compared with that of SnO₂ gas sensor, indicating an improved selectivity property. The other three ZSM-5 zeolites with SiO₂/Al₂O₃ 70, 150 and 470, respectively, and grain sizes all around 1 μm coated SnO₂ sensors did not show much difference with SnO₂ sensor for the response properties to both formaldehyde and acetone. The sensing mechanism of ZSM-5 modified sensors was briefly analyzed.
منابع مشابه
Improving Gas Sensing Properties of Tin Oxide Nanowires Palladium-Coated Using a Low Cost Technique
Thin films of SnO2 nanowires were successfully prepared by using chemical vapor deposition (CVD) process on quartz substrates. Afterwards, a thin layer of palladium (Pd) as a catalyst was coated on top of nanowires. For the deposition of Pd, a simple and low cost technique of spray pyrolysis was employed, which caused an intensive enhancement on the sensing response of fabricated sensors...
متن کاملEffect of Particle Size of NaX Zeolite on Adsorption of CO2/CH4
In the present work, the nano-NaX zeolite and micro-NaX zeolite were synthesized via hydrothermal method. Then, the adsorption capacities and isotherms of pure gases CO2 and CH4 on the synthesized zeolite nanoparticles were determined at three temperatures of 288, 298 and 308 K and various pressures from 1 up to 20 bar. Adsorption capacities of CO2 on the nano-sized zeolites NaX were showed to ...
متن کاملSynthesis of zeolite NaA nano-crystalls; effect of synthesis parameters on crystallinity and crystal size
Abstract In this work hydrothermal synthesis of zeolite NaA crystals with a composition of Al2O3:aSiO2:bNa2O:cH2O was investigated. Effects of SiO2/Al2O3, Na2O/Al2O3 and H2O/Al2O3 ratios and crystallization temperature and time were studied on crystallinity and crystal size of zeolite NaA crystals. It was tried to understand the interactions between these parameters. The crystal species o...
متن کاملExploitation of Unique Properties of Zeolites in the Development of Gas Sensors
The unique properties of microporous zeolites, including ion-exchange properties, adsorption, molecular sieving, catalysis, conductivity have been exploited in improving the performance of gas sensors. Zeolites have been employed as physical and chemical filters to improve the sensitivity and selectivity of gas sensors. In addition, direct interaction of gas molecules with the extraframework ca...
متن کاملSynthesis, characterization, and gas sensing properties of In-doped ZnO nanopowders
Indium (1at %) doped ZnO and ZnO nanoparticles have been synthesized via sol gel method. The structural characters of the synthesized nanoparticles have been studied by X-ray diffraction pattern (XRD), scanning electron microscopy (SEM) and energy-dispersiveX-ray spectroscopy (EDX). From synthesized nanopowders a tablet was prepared by using the isostatic pressing and then sintered at ...