Modified Nanocrystalline Cellulose from Two Kinds of Modifiers Used for Improving Formaldehyde Emission and Bonding Strength of Urea- Formaldehyde Resin Adhesive

نویسندگان

  • Hao Zhang
  • Jing Zhang
  • Shuping Song
  • Guofeng Wu
چکیده

In this study, nanocrystalline cellulose (NCC) was used for increasing the bonding strength of urea-formaldehyde (UF) resin adhesive, with a reduction of formaldehyde (HCHO) emissions. The surface of NCC was modified by 3-aminpropyltriethoxysilane (APTES) and 3-methacryloxypropyltrimethoxysilane (MPS) for the lack of compatibility with UF resin adhesive. The modified NCC was characterized by X-ray powder diffraction (XRD), thermogravimetric analysis (TG), and wetting property. HCHO emission and bonding strength of the UF resin adhesive with modified NCC were tested according to Chinese National Standards GB/T 17657-1999 and GB/T 9846-2004. The results of XRD, TG, and wetting property from NCC modified by APTES showed more significant improvements than that from NCC modified by MPS. The HCHO emission of UF resin adhesive with 1.5% NCC modified by APTES decreased by 53.2% and bonding strength increased by 23.6%, while the results from the NCC modified by MPS were 21.3% and 7.0%, respectively.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Properties of Particleboard Made from UF with Low-formaldehyde (E1) (TECHNICAL NOTE)

The objective of this study was to manufacture particleboard made from UF with low formaldehyde (E1) for use in indoor environments. The influence of UF in particles on the formaldehyde emission and its mechanical properties were investigated. The experimental results showed that the formaldehyde emission released decreased linearly with consumption UF-low formaldehyde- particle. Formaldehyde e...

متن کامل

Sand Production Control in Sandstone Reservoirs Using a Modified Urea-formaldehyde Re

Several techniques have been used for sand production control in sandstone reservoirs.The main objective of this research is to present a suitable resin to be used as a consolidation agent in oil reservoirs. To achieve this purpose, urea-formaldehyde resin, phenol-formaldehyde resin, and modified urea-formaldehyde resin were selected to be studied. Core samples were made by the sand sample prov...

متن کامل

Characteristics on indoor air pollutant emission from wood-based flooring by environmental-friendly natural adhesive using CNSL

To discuss the reduction of formaldehyde and volatile organic compound (VOC) emissions from engineered flooring, cashew nut shell liquid (CNSL)-formaldehyde (CF) resin and CF/PVAc resin were applied for the maple face of the veneer bonding on plywood. The CF resin was used to replace urea-formaldehyde (UF) resin in the formaldehyde-based resin system in order to reduce formaldehyde and VOC emis...

متن کامل

Melamine-Bridged Alkyl Resorcinol Modified Urea– Formaldehyde Resin for Bonding Hardwood Plywood

A powdery product was obtained by the reaction of methylolated melamine with alkyl resorcinols to form melamine-bridged alkyl resorcinols (MARs). The effects of the addition of this powder on the bonding strength and formaldehyde emission of urea–formaldehyde (UF) resins were investigated. Three types of UF resins with a formaldehyde/urea molar ratio of 1.3 synthesized by condensation at pH 1.0...

متن کامل

Melamine-modified urea formaldehyde resin for bonding particleboards

For the development of a cost-effective melamine-modified urea formaldehyde resin (MUF), the study evaluated the effects of reaction pH and melamine content on resin properties and bond performance of the MUF resin adhesive systems. Eight resins, each with three replicates, were prepared in a factorial experiment that included two formulation variables: two reaction pHs (i.e., 4.5 and 8.0) and ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2011