A computational damage mechanics model for thermomigration
نویسندگان
چکیده
Miniaturization of electronics to nanoscale leads to significantly higher current density levels and larger thermal gradients in electronics packaging. Laboratory test data show that thermomigration plays a significant role in high current density induced failure in solder joints and interconnects. In this paper, a computational damage mechanics model for thermomigration process is proposed and implemented in finite element method. This model is based on thermodynamics and formulated by continuum mechanics equations, mass transport principals and heat transfer equations. A damage evolution model using entropy production rate as a metric is utilized to evaluate the degradation in solder joints subjected to high temperature gradients. 2008 Elsevier Ltd. All rights reserved.
منابع مشابه
Simulating Damage Mechanics of Electromigration and Thermomigration
Electromigration (EM) and thermomigration (TM) are processes of mass transport which are critical reliability issues for next generation nanoelectronics and power electronics. The purpose of this project is to develop a computational tool for simulating damage mechanics of EM and TM and their interaction. In this paper, a model for EM and TM processes is proposed and has been implemented in a g...
متن کاملComputational damage mechanics of electromigration and thermomigration
Articles you may be interested in Thermomigration and electromigration in Sn58Bi solder joints Electromigration in flip chip solder joints having a thick Cu column bump and a shallow solder interconnect Effect of entropy production on microstructure change in eutectic SnPb flip chip solder joints by thermomigration Appl. Reliability of solder joints under Electromigration (EM) and Thermomigrati...
متن کاملJoints under Electric Current Stresses Experimental Damage Mechanics of Micro / Power Electronics Solder
Experimental damage mechanics of flip chip solder joints under current stressing is studied using 20 test vehicle flip chip modules. Three different failure modes are observed. The dominant damage mechanism is caused by the combined effect of electromigration and thermomigration, where void nucleation and growth lead to the ultimate failure of the module. It is observed that thermomigration dri...
متن کاملA damage model incorporating dynamic plastic yield surface
In this paper, a general elastoplastic-damage constitutive model considering the effect of strain rate has been developed. The derivation of this model has been cast into the irreversible thermodynamics with internal variables within the fundamentals of Continuum Damage Mechanics (CDM). The rate effect has been involved as an additional term into the plastic yield surface (dynamic plastic yield...
متن کاملDuctile Damage Evolution under Triaxial Stress Conditions: Computational and Experimental Evaluations
The continuum mechanic simulation of micro-structural damage process is important in the study of ductile fracture mechanics. In this paper, the continuum damage mechanics model formulation proposed by Lematire has been validated against ductile damage evolution experimentally measured in A533B-C1 steel under stress triaxiality conditions. First, a 
procedure to identify the model parameters...
متن کامل