Anodizing of Magnesium Alloy Az31 by Alkaline Solution
نویسندگان
چکیده
-Anodizing of AZ 31 Mg alloy was investigate in 3M KOH solution for 10, 20 and 30min. at constant voltage of 5V. Atomic force microscope (AFM) used to investigate the roughness of anodic film formed on the surface while the scanning electron microscope (SEM) was used to determine the morphology of the anodic film, it was found that the roughness of the anodic film is mainly depend on the anodizing time. Coating thickness. Furthermore, the microhardness also increases with the anodizing time.
منابع مشابه
Carbon nanotubes reinforced electrospun chitosan nanocomposite coating on anodized AZ31 magnesium alloy
Chitosan based nanofibers containing carbon nanotubes were applied on AZ31 magnesium alloy via electrospinning. The magnesium substrate was initially anodized in a NaOH solution in order to improve the adhesion between the coating and substrate. Electrospinning parameters were optimized and homogenous nanofibers composite coatings were produced. Addition of carbon nanotubes reduced the size of ...
متن کاملEffect of Mucin and Bicarbonate Ion on Corrosion Behavior of AZ31 Magnesium Alloy for Airway Stents
The biodegradable ability of magnesium alloys is an attractive feature for tracheal stents since they can be absorbed by the body through gradual degradation after healing of the airway structure, which can reduce the risk of inflammation caused by long-term implantation and prevent the repetitive surgery for removal of existing stent. In this study, the effects of bicarbonate ion (HCO₃-) and m...
متن کاملCharacterisation and Corrosion Performance of MultilayerNano Nickel Coatings on AZ31 Magnesium Alloy
Ni-P and Ni layers multilayer coatings were applied to AZ31 magnesium alloy utilizing electroless and electrodeposition procedures. The aim of the project was to decrease cracks and increase corrosion resistance of the coatings. In order to compare the coatings, the effect of single layer electroless Ni-P coatings with different thicknesses was also investigated. The microstructure and phase co...
متن کاملCorrosion behaviour of AZ31 magnesium alloy with different grain sizes in simulated biological fluids.
The corrosion behaviour of AZ31 magnesium alloy with different grain sizes immersed in simulated body fluids was compared in chloride solution (8 gl(-1)) and in phosphate-buffer solution (PBS). The influence of immersion time was also analyzed. Electrochemical techniques such as open circuit potential, polarization curves, transient currents and electrochemical impedance spectroscopy, complemen...
متن کاملCorrosion Resistance of the Superhydrophobic Mg(OH)2/Mg-Al Layered Double Hydroxide Coatings on Magnesium Alloys
Coatings of the Mg(OH)2/Mg-Al layered double hydroxide (LDH) composite were formed by a combined co-precipitation method and hydrothermal process on the AZ31 alloy substrate in alkaline condition. Subsequently, a superhydrophobic surface was successfully constructed to modify the composite coatings on the AZ31 alloy substrate using stearic acid. The characteristics of the composite coatings wer...
متن کامل