Highly oriented LiFePO4 thin film electrodes via chemical solution deposition
نویسندگان
چکیده
Highly oriented LiFePO4 thin-film electrodes were fabricated via chemical solution deposition combined with spin coating. The effects of the precursor concentrations and types of substrates on microstructures and electrochemical performances were studied. Single-phase LiFePO4 with orientations perpendicular to the (211)/(020) and (311) planes prepared using stainless steel as substrate presents the capacity of 4.9 μAh•cm-2 and the apparent activation energy of 59.2 kJ•mol-1, indicating its great potential to be used as cathode material for lithium thin film batteries.
منابع مشابه
Synthesis of Boron-Aluminum Nitride Thin Film by Chemical Vapour Deposition Using Gas Bubbler
Boron included aluminium nitride (B-AlN) thin films were synthesized on silicon (Si) substrates through chemical vapour deposition ( CVD ) at 773 K (500 °C). tert-buthylamine (tBuNH2) solution was used as nitrogen source and delivered through gas bubbler. B-AlN thin films were prepared on Si-100 substrates by varying gas mixture ratio of three precursors. The structural properties of the films ...
متن کاملCharacterization and Performance of LiFePO4 Thin-Film Cathodes Prepared with Radio-Frequency Magnetron-Sputter Deposition
Characterization and Performance of LiFePO4 Thin-Film Cathodes Prepared with Radio-Frequency Magnetron-Sputter Deposition Jian Hong,* Chunsheng Wang,** Nancy J. Dudney,** and Michael J. Lance Department of Chemical Engineering, Tennessee Technological University, Cookeville, Tennessee 38505, USA Department of Chemical and Biochemical Engineering, University of Maryland, College Park, Maryland 2...
متن کاملChemical solution deposition of the highly c-axis oriented apatite type lanthanum silicate thin films.
Highly c-axis oriented apatite-type lanthanum silicate (LSO) thin films were fabricated by a simple solution coating method. In the solution coating method, LSO thin films are obtained by crystallization of initially deposited amorphous LSO precursor thin films. The degree of orientation was influenced by the precursor morphologies and a dense LSO precursor led to a high c-axis orientation perp...
متن کاملPreparation of Nanocrystalline CdS Thin Films by a New Chemical Bath Deposition Route for Application in Solar Cells as Antireflection Coatings
Nanocrystalline cadmium sulfide thin films as antireflection materials for solar cells have been prepared by a new chemical solution deposition route in an aqueous medium at 50 °C. as-deposited thin films were studied using X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and optical absorption spectra. X-ray diffraction data indicated the formation of hexagonal na...
متن کاملStructural and Electrochemical Properties of LiNi0.5Mn0.5O2 Thin-Film Electrodes Prepared by Pulsed Laser Deposition
LiNi0.5Mn0.5O2 thin-film electrodes have been prepared by pulsed laser deposition followed by postannealing at different temperatures. The microstructural and morphological characterizations using X-ray diffraction, field-emission-scanning electron microscopy, and Raman spectroscopy measurements show that the structure and phase purity of the thin films are highly dependent on the postannealing...
متن کامل