Effect of B and Cr on Mechanical Properties and Magnetostriction of Iron-Gallium Alloy
نویسندگان
چکیده
Effects of B and Cr additions on magnetostriction and the mechanical properties of polycrystalline Fe83Ga17 alloy were investigated. Small addition of B increased magnetostriction of Fe83Ga17 alloy slightly, and improved the room temperature ductility and tensile strength significantly. The elongation and tensile strength of the (Fe83Ga17)99B1 alloy increased to 3.56% and 548MPa compared with that of Fe83Ga17 alloy respectively. The Cr addition was shown to improve the room temperature mechanical properties of Fe83Ga17 alloy beneficially. The maximum magnetostriction of (Fe83Ga17)98Cr2 alloy was 70 10 . The influences of B and Cr additions on the fracture mode of Fe83Ga17 alloy were also studied in this paper. [doi:10.2320/matertrans.M2009061]
منابع مشابه
Effect of Mechanical Alloying and Sintering on Phase Transformation, Microstructural Evolution, Mechanical Properties and Density of Zr-Cr Alloy
The purpose of present research was production ofZr-based alloy as the nuclear fuel cladding by mechanical alloying (MA) and sintering process. Firstly, Zr and Cr powders were mechanically alloyed to produce the refractory and hard Zr-10 wt% Cr alloy, and then, the powder mixtures were consolidated by press and following sintering at temperature of 800˚C min. The phase evolution, microstructura...
متن کاملProduction of Cu-Cr-Zr Alloy Using Electro Slag Remelting Technique (RESEARCH NOTE)
This study focused on the effect of electro slag remelting process (ESR) on microstructure and composition of an as-cast alloy of Cu-Cr-Zr. These observations revealed that applying ESR process results in a more uniform distribution of alloying elements, however a slight aggregation of large precipitates and inclusions existed in as-cast ingot was found. Additionally, impurities like P, S and M...
متن کاملStructural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کاملSynthesis of Nanostructure Ti-45Al-5Cr Alloy by Mechanical Alloying and Study the Effect of Cr Addition on Microstructure of TiAl Alloy
In this work, mechanical alloying was employed to produce Ti-50Al and Ti-45Al-5Cr (at%) alloys. Alloying was performed in a planetary mill and the alloying time varying from 5 to 70h. Characterization of the powder mixture was performed by X-ray diffraction (XRD), SEM analyses and DTA test, during mechanical alloying and after annealing at 1100°c in vacuum oven. The results showed, after 50h of...
متن کاملProduction and Characterization of Nano Crystalline Fe85Si10Ni5 Soft Magnetic Alloys by Mechanical Alloying
Abstract There are various methods to produce iron based nano crystalline magnetic alloys. Among these methods, mechanical alloying is one of the most important. In this research, nano crystalline Fe85Si10Ni5 soft magnetic alloy was synthesized by mechanical alloying. The effect of alloying time on phase constituents and magnetic properties of the produced powders was investigated, by X-ray di...
متن کامل