Preparation and characterization of ZnS:Cu/PVA composite nanofibers via electrospinning

نویسندگان

  • Haiying Wang
  • Xiaofeng Lu
  • Yiyang Zhao
  • Ce Wang
  • Alan G. MacDiarmid
چکیده

ZnS:Cu/Poly(vinyl alcohol) (PVA) composite nanofibers have been successfully prepared by electrospinning technique. The formation of ZnS: Cu/PVA nanofibers were carried out by reacting H2S with Zn(AC)2:Cu/PVA nanofibers, which were electrospun from the mixture aqueous solution of Zn(Ac)2, Cu(Ac)2 and PVA. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray-diffraction (XRD) analyses revealed that the morphology of the ZnS:Cu/PVA nanofibers consists of the dispersion of ZnS:Cu nanopaticles with cubic structure in PVA nanofibers. The coordinations between –OH and Zn:Cuwere characterized by infrared spectroscopy. The photoluminescence spectroscopy studies showed the significant difference between the ZnS/PVA fibers and the ZnS:Cu/PVA fibers. The luminescence decay time measure further invested that the Cu was doped in the ZnS crystal. © 2006 Elsevier B.V. All rights reserved.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Preparation and Characterization of Aligned and Random Nanofibrous Nanocomposite Scaffolds of Poly (Vinyl Alcohol), Poly (e-Caprolactone) and Nanohydroxyapatite

Nanofibrous scaffolds produced by electrospinning have attracted much attention, recently. Aligned and random nanofibrous scaffolds of poly (vinyl alcohol) (PVA), poly (ε-caprolactone) (PCL) and nanohydroxyapatite  (nHA) were fabricated by electrospinning method in this study. The composite nanofibrous scaffolds were subjected to detailed analysis. Morphological investigations revealed that the...

متن کامل

Carboxymethylchitosan nanofibers containing silver nanoparticles: Preparation, Characterization and Antibacterial activity

Article history: Received on: 28/01/2016 Revised on: 17/03/2016 Accepted on: 18/05/2016 Available online: 28/07/2016 Herein we prepare antibacterial composite from carboxymethylchitosan (CMCS) nanofibers and silver nanoparticles (AgNPs) by using poly (vinyl alcohol) (PVA) as reducing, capping and fiber aiding material and investigated to be used in biomedical applications. The AgNPs has spheric...

متن کامل

Fabrication of Compound Nanofibers For Antibacterial Applications in Filtration

In the present study, fabrication and characterization of compound composite nanofibers of Polyvinyl Alcohol (PVA) with nano silver and Polyamide 6 (PA6) are demonstrated. Compound composite fibers with core-shell structure were made using co-axial electrospinning method. The shell was made up of nano silver (Ag) impregnated PVA while PA6 was the core material. These compound composite nanofibe...

متن کامل

Nanofiber composites of polyvinyl alcohol and cellulose nanocrystals: manufacture and characterization.

Cellulose nanocrystals (CN) were used to reinforce nanofibers in composite mats produced via electrospinning of poly(vinyl alcohol) (PVA) with two different concentrations of acetyl groups. Ultrathin cross-sections of the obtained nanocomposites consisted of fibers with maximum diameters of about 290 nm for all the CN loads investigated (from 0 to 15% CN loading). The electrospinning process di...

متن کامل

بررسی خواص ساختاری و مغناطیسی الیاف ابررسانای YBa2Cu3O7- ساخته شده به‌روش الکتروریسندگی

Electrospinning is one of the most feasible techniques for producing nanoceramic fibers. In this paper, YBa2Cu3O7-δ (YBCO) superconductor nanofibers synthesized using electrospinning. The first step was preparation of a composite that is formed by mixing yttrium, barium, and copper acetates with different percent of polyvinyl alcohol (PVA). Then, the composite polymer has been electrospun to pr...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2006