Microstructure and Mechanical Behavior of Porous Ti–6Al–4V Processed by Spherical Powder Sintering
نویسندگان
چکیده
Reducing the stiffness of titanium is an important issue to improve the behavior of this material when working together with bone, which can be achieved by generating a porous structure. The aim of this research was to analyze the porosity and mechanical behavior of Ti-6Al-4V porous samples developed by spherical powder sintering. Four different microsphere sizes were sintered at temperatures ranging from 1300 to 1400 °C for 2, 4 and 8 h. An open, interconnected porosity was obtained, with mean pore sizes ranging from 54.6 to 140 µm. The stiffness of the samples diminished by as much as 40% when compared to that of solid material and the mechanical properties were affected mainly by powder particles size. Bending strengths ranging from 48 to 320 MPa and compressive strengths from 51 to 255 MPa were obtained.
منابع مشابه
An Overview of Densification, Microstructure and Mechanical Property of Additively Manufactured Ti-6Al-4V — Comparison among Selective Laser Melting, Electron Beam Melting, Laser Metal Deposition and Selective Laser Sintering, and with Conventional Powder Metallurgy
This chapter begins with an introduction of the fundamental properties of Ti-6Al-4V, and its densification mechanism, typical microstructure and mechanical property achievable by conventional PM routes. This functions as a point of reference for the following discussion of the AM Ti-6Al-4V in terms of densification, microstructure, and mechanical property. The mostly popular laser-based AM tech...
متن کاملCharacterization of the microstructure, tensile and creep behavior of powder metallurgy processed and rolled Ti-6Al-4V-1B Alloy
This work investigated the microstructure and elevated-temperature (400-475C) tensile and tensile-creep deformation behavior of a powder metallurgy (PM) rolled Ti-6Al-4V-1B(wt.%) alloy. The PM rolled Ti-6Al-4V-1B alloy exhibited a duplex microstructure, and it did not exhibit a strong α-phase texture compared with the PM extruded Ti-6Al-4V-1B alloy. The PM rolled Ti6Al-4V-1B alloy exhibited gre...
متن کاملMicrostructure and Mechanical Properties of Direct Metal Laser Sintered Ti- 6al-4v
Direct metal laser sintering (DMLS) is a selective laser melting (SLM) manufacturing process that can produce near net shape parts from metallic powders. A range of materials are suitable for SLM; they include various metals such as titanium, steel, aluminium, and cobalt-chrome alloys. This paper forms part of a research drive that aims to evaluate the material performance of the SLM-manufactur...
متن کاملTi-6Al-4V Synthesized by Mechanical Alloy Method and Mechanical and Bioactivity Properties of Ti-6Al-4V/HA-Clay Nano composite
Nowadays, titanium-based alloys are among the most attractive metallic materials for biomedical applications (as implants) due to their non-biodegradability, low density, good mechanical properties as well as their good biocompatibility. Hydroxyapatite (Ca10 (PO4)6(OH)2, HA) has been widely used for biomedical applications due to its bioactive, biocompatible and osteoconductive properties. Firs...
متن کاملMechanical behaviour of pressed and sintered titanium alloys obtained from prealloyed and blended elemental powders.
The applicability of irregular prealloyed Ti-6Al-4V powder for the fabrication of titanium products by pressing and sintering and its employment as a master alloy to obtain the Ti-3Al-2.5V alloy was studied. To this end, the starting powders were characterised by dilatometry, differential thermal analysis and XRD. Green samples were obtained by cold uniaxial pressing, and the evolution of the m...