Simulation of Acoustic Properties of Borate and Tellurite Glasses
نویسندگان
چکیده
Makishima and Mackenzie model was used to simulation of acoustic properties (longitudinal and shear ultrasonic wave velocities, elastic moduli theoretically for many tellurite and borate glasses. The model was proposed mainly depending on the values of the experimentally measured density, which are obtained before. In this search work, we are trying to obtain the values of densities of amorphous glasses (as the density depends on the geometry of the network structure of these glasses). In addition, the problem of simulating the slope of linear regression between the experimentally determined bulk modulus and the product of packing density and experimental Young's modulus, were solved in this search work. The results showed good agreement between the experimentally measured values of densities and both ultrasonic wave velocities, and those theoretically determined. Keywords---Glasses, ultrasonic wave velocities, elastic moduli, Makishima and Mackenzie model.
منابع مشابه
Structural Investigation, Physical and Optical Properties of Mixed Alkali Bismuth Borate Glasses
Lead free, eco-friendly bismuth borate glasses doped with alkali oxides of composition xLi2O+(30-x)Na2O+55B2O3+15Bi2O3 (x = 5,10,15,20,25) were prepared by melt quenching technique. Amorphous nature of glasses was confirmed by X-ray diffraction. Density measurements were carried out at room temperature by standard principle of Archimedes with Xylene as an immersion liquid. The non-linear ...
متن کاملLuminescence Properties of TeO2-LiF-Gd2O3 Glasses
In this work, the structural properties and spectroscopic behavior 80 mol.%TeO2-20mol.%LiF glasses which were doped with 0. 05, 0. 2 mole% Gd2O3 have been studied. It was shown that, by increasing the amount of Gd2O3 the glass stability was decreased. The PL emissions at 431nm and 627nm wavelengths were distinguished by 320nm excitation. The FT-IR analysis showed deformed TeO4 groups in these ...
متن کاملLuminescence Enhancement in Eu(III)-Doped Tellurite Glass Embedded Silver Nanoparticles
Introduction of the metallic nanoparticles (NPs) in the bulk glass received a large interest due to their versatile applications. The effect of silver NPs on optical properties of the Eu3+-doped zinc tellurite glasses is presented for the first time. Glass samples are prepared by melt-quenching technique. The surface plasmon absorption bands of silver NPs are recorded in the visible ...
متن کاملX-ray Absorption Fine Structure (XAFS) Studies of Oxide Glasses—A 45-Year Overview
X-ray Absorption Fine Structure (XAFS) spectroscopy has been widely used to characterize the short-range order of glassy materials since the theoretical basis was established 45 years ago. Soon after the technique became accessible, mainly due to the existence of Synchrotron laboratories, a wide range of glassy materials was characterized. Silicate glasses have been the most studied because the...
متن کاملHost dependent frequency upconversion of Yb3+/Tm3+-codoped oxyfluoride tellurite glasses
The upconversion luminescence properties of Yb3+/Tm3+-codoped oxyfluoride tellurite glasses under 980 nm excitation are investigated experimentally. The intense blue and relatively weak red emissions centered at 475 and 649 nm corresponding to the transitions G4 → H6 and 1
متن کامل