Compressive Strength of Mineral Trioxide Aggregate and Calcium-enriched Mixture Cement Mixed with Propylene Glycol

Introduction The aim of the present study was to evaluate and compare the compressive strength (CS) of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cement when mixed with propylene glycol (PG). Methods and Materials Twenty four custom-made split molds with 5 holes in each were prepared. Molds were allocated into eight groups (n=15 holes) as follows: Groups 1,5: CEM and MTA mixed with PG (100%), Groups 2,6: CEM and MTA mixed with PG (20% )+CEM or MTA liquid (80%) respectively, Groups 3,7: CEM and MTA mixed with PG (50% )+CEM or MTA liquid (50% ) respectively, Groups 4,8: CEM and MTA mixed with CEM or MTA liquid respectively as control groups. All specimens were kept in 37°C in an incubator and the compressive strength was evaluated after 7 days. Data were analyzed using the Kruskal Wallis and Dunne tests. The level of significance was set at 0.05. Results In all concentration of PG, MTA samples showed better results than CEM cement. In CEM samples, adding 20% PG could significantly increase the compressive strength in comparison with control group and 100% PG (P=0.047 and P=0.011, respectively). In MTA samples, adding 100% and 50% PG significantly increased the compressive strength of the cement in comparison with control group (P=0.037 and, P=0.005, respectively). Conclusion Considering the limitations of the present study, appropriate concentration of PG could improve the CS of MTA and CEM cement.