Preparation and Characterization of MoB Coating on Mo Substrate
نویسندگان
چکیده
A molybdenum boride (MoB) coating was prepared on molybdenum (Mo) by an in-situ chemical vapor deposition method. To develop a fuller understanding of the effect of depositional conditions on the growth of MoB coating formed on Mo substrate, this paper studied the phase composition and microstructure of the coating at varied conditions. At the same time, the relationships between the growth of the coating in thickness and depositional conditions were also investigated. The phase composition of the coating, which was prepared using 0.2 wt % boron (B), was composed of MoB and Mo2B phases. The single MoB phase was obtained using a high B content (above 0.2 wt %). The microstructure of the coating showed that MoB coating could be prepared at temperatures over 900 ◦C. With the increase of temperature and time, the thickness of the coating increased. The growth of the coating was also influenced by the content of NaF. With increasing content, the thickness of the coating first increased, and then decreased. In addition, the prepared coating had a high hardness (3130.85 HV), and the mass change of the coated sample was only 4.92 mg/cm2 after isothermal oxidation at 600 ◦C for 100 h. The MoB coating could provide a good oxidation resistance for Mo at 600 ◦C.
منابع مشابه
Preparation and Characterization of Hydroxyapatite Coating on Ti6Al4V Cylinders by Combination of Alkali-Heat Treatments and Biomimetic Method
Biomimetic method was used to apply hydroxyapatite (HA) coating onto Ti6Al4V cylinders. This process is a physicochemical method in which a substrate is soaked in a solution simulating the physiological conditions, for a period of time enough to form a desirable layer of the calcium phosphate on the substrate. In the present study, specimens were soaked in 5, 10 M solutions of NaOH at temperatu...
متن کاملPreparation and Characterization of WO3 Electrochromic Films Obtained by the Sol-Gel Process
Tungsten trioxide (WO3) films have been coated on indium thin oxide (ITO) conductive glass substrate, using aqueous solution of peroxotungstic acid (PTA) by the sol-gel dip coating method. X-ray diffractometery (XRD) analysis confirmed monoclinic and triclinic structure for the film and powdered WO3 respectively. Fourier transforms infrared spectroscopy (FT-IR) exhibit...
متن کاملPreparation of thin layer of TiO2 on glazed tile substrate and changing hydrophilic to hydrophobicity behavior
The aim of this study is to create TiO2 coating on the tile substrate using cell-gel and immersion method. Initially, TiO2 coating was prepared by sol gel method and then, deposition was performed in three stages with different immersion periods of 20, 40 and 60 s and finally, the samples were calcined at 450 °C. The phases and microstructural characteristics of the samples were analyzed using ...
متن کاملNanocomposite Coating Based on Thermoplastic Acrylic Resin and Montmorillonite Clay: Preparation and Corrosion Prevention Properties
Different amounts of nanoclay were incorporated into the acrylic resin matrix at 0, 1, 3, and 5 wt.% loadings. The coatings were applied on low carbon steel plates. Optical microscopy, sedimentation test, transmission electron microscopy, and X-ray diffraction were employed to investigate the dispersion of nanoclay in matrix. The corrosion resistance of coatings was evaluated by electrochemical...
متن کاملSurface Characterization and Tribological Behaviour of Ti-Ni-P Intermetallic Coatings on Titanium Alloys
In this research, tribological behavior of Ti-Ni-P intermetallic coatings on titanium substrates have been investigated under dry reciprocating conditions. Hardness profile testing results exhibit that high surface hardness has been attained and static indentation result shows that the intermetallic coating has better adhesion strength than the conventional ceramic coatings. In this respect, th...
متن کامل