Corrosion Properties of F82H in Flowing High Temperature Pressurized Water
نویسندگان
چکیده
This work reports the effects of water flow and dissolved oxygen (DO) on corrosion behavior of reduced activation ferritic/martensitic steel, F82H. The corrosion tests were performed in high temperature pressurized water by using a test apparatus for rotated disk sample. All of specimens showed weight gains after static corrosion tests up to 500 h. However, the rotated disk showed weight losses except for test in the water with DO=8 ppm, and the weight loss was significant with lowering DO concentration.
منابع مشابه
Boric Acid Corrosion of Concrete Rebar
Borated water leakage through spent fuel pools (SFPs) at pressurized water reactors is a concern because it could cause corrosion of reinforcement steel in the concrete structure and compromise the integrity of the structure. Because corrosion rate of carbon steel in concrete in the presence of boric acid is lacking in published literature and available data are equivocal on the effect of boric...
متن کاملExperimental Results of Pressure Fluctuations in a Water Conduit Section Due to Formation of Unstable Two-Phase Air-Water Flow
The study of two-phase fluid flow behavior in hydraulic structures such as pressurized flow tunnels, culverts, sewer pipes, junctions and other similar conduits is of great importance. A two-phase mixture flowing in a pipe can exhibit several interfacial geometries such as bubbles, slugs or films, depending on the fluid and hydrodynamic properties of flow. The main variables, giving rise to a v...
متن کاملExperimental Results of Pressure Fluctuations in a Water Conduit Section Due to Formation of Unstable Two-Phase Air-Water Flow
The study of two-phase fluid flow behavior in hydraulic structures such as pressurized flow tunnels, culverts, sewer pipes, junctions and other similar conduits is of great importance. A two-phase mixture flowing in a pipe can exhibit several interfacial geometries such as bubbles, slugs or films, depending on the fluid and hydrodynamic properties of flow. The main variables, giving rise to a v...
متن کاملA study on corrosion and scaling potential of drinking water supply resources in rural areas of Sarvabad, West of Iran
Corrosion is a physicochemical reaction occurring between the metal and its surroundings, which usually has an electrochemical nature and results in changes in the properties of the metal. The corrosive water dissolves the pipe’s material during flowing and this causes many problems. This study investigated the potential of corrosion and scaling of 46 water supply resources in the villages of S...
متن کاملPolymer Impregnation of Concrete by Methyl Methacrylate and its Effects on Mechanical Properties and Corrosion of Steel in Concrete
Freezing and thawing resulting from the ingression of water into concrete causes cracking or spalling. Corrosive ions such as chloride or sulfate penetrate the concrete surface and eventually reach the reinforcing steel. This causes the steel to corrode. Because of the high maintenance and replacement costs, responsible officials should be increasingly concerned about the growing number...
متن کامل