Additive manufactured Ti6Al4V scaffolds with the RF- magnetron sputter deposited hydroxyapatite coating
نویسنده
چکیده
Present paper reports on the results of surface modification of the additively manufactured porous Ti6Al4V scaffolds. Radio frequency (RF) magnetron sputtering was used to modify the surface of the alloy via deposition of the biocompatible hydroxyapatite (HA) coating. The surface morphology, chemical and phase composition of the HA-coated alloy were studied. It was revealed that RF magnetron sputtering allows preparing a homogeneous HA coating onto the entire surface of scaffolds.
منابع مشابه
Investigation of the HA film deposited on the porous Ti6Al4V alloy prepared via additive manufacturing
This study is focused on the use of radio frequency magnetron sputtering to modify the surface of porous Ti6Al4V alloy fabricated via additive manufacturing technology. The hydroxyapatite (HA) coated porous Ti6Al4V alloy was studied in respect with its chemical and phase composition, surface morphology, water contact angle and hysteresis, and surface free energy. Thin nanocrystalline HA film wa...
متن کاملA Study of the Tribological Properties of Sputter-deposited MoSX/Cr Coatings
In this investigation, MoSx/Cr coatings were deposited by direct-current magnetron sputter onto Ck45 (AISI 1045) plain carbon steel substrates. The MoSx/Cr ratio in the coatings was controlled by sputtering the composite targets. The chemical characterization was performed using EDX (energy dispersive X-ray analysis); the structural characterization was accomplished by X-ray diffraction (XRD) s...
متن کاملStrontium-substituted hydroxyapatite coatings deposited via a co-deposition sputter technique.
The bioactivity of hydroxyapatite (HA) coatings can be modified by the addition of different ions, such as silicon (Si), lithium (Li), magnesium (Mg), zinc (Zn) or strontium (Sr) into the HA lattice. Of the ions listed here, strontium substituted hydroxyapatite (SrHA) coatings have received a lot of interest recently as Sr has been shown to promote osteoblast proliferation and differentiation, ...
متن کاملPhysical Properties of Reactively Sputter-Deposited C-N Thin Films
This work aims to prepare and study amorphous carbon nitride (CNx) films. Films were deposited by reactive magnetron radiofrequency (RF) sputtering from graphite target in argon and nitrogen mixture discharge at room temperature. The ratio of the gas flow rate was varied from 0.1 to 1. Deposited films were found to be amorphous. Highest Nitrogen concentration achieved was 42 atomic percent whic...
متن کاملInfluence of the Substrate Bias Voltage on the Crystallographic Structure and Surface Composition of Ti6A14V Thin Films Deposited by rf Magnetron Sputtering
In this work, the influence of the substrate bias on the crystalline structure and surface composition of Ti6Al4V thin films prepared by rf magnetron sputtering were studied. Samples were grown onto two different types of substrates: AISI 420 steel and common glass using a Ti6Al4V (99.9 %) target. Substrate bias was varied from –100V to –200 V. Samples were characterized by X-ray diffraction (X...
متن کامل