Properties of Ni and Ni–Fe nanowires electrochemically deposited into a porous alumina template
نویسندگان
چکیده
The comparative analysis of the electrochemical deposition of Ni and Ni-Fe nanowires (NWs) into ordered porous alumina templates is presented. The method developed allows for obtaining NWs of 50 ± 5 nm in diameter and 25 μm in length, i.e., with an aspect ratio of 500. XRD data demonstrate the polycrystalline nature of Ni and Ni-Fe in a face-centered cubic close-packed lattice. Both fabricated materials, Ni and Ni-Fe, have shown ferromagnetic properties. The specific magnetization value of Ni-Fe NWs in the alumina template is higher than that of the Ni sample and bulk Ni, also the Curie temperature of the Ni-Fe sample (790 K) is higher than that of the Ni sample one or bulk Ni.
منابع مشابه
Magnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملThe effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the CoNi nanowires
CoNi nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. The effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the CoNi nanowires were investigated. Maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. The coerciv...
متن کاملنقش ناهمسانگردیهای بلوری و شکلی بر خواص مغناطیسی نانوسیمهای کبالت و نیکل
Co and Ni magnetic nanowires with different diameter and deposition time were fabricated into the alumina template using ac electrodeposition. For Ni nanowires with 30 nm diameter the coercivity initially increased then dropped with deposition time, while it only increased with deposition time for all the other diameters. In general, the results showed that the coercivity reduced with diamete...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy. We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relation ...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy.
 We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relatio...
متن کامل