Field Emission Studies of Heat Treated Mo Substrates
نویسندگان
چکیده
Molybdenum can be used as a substrate for bi-alkali antimonide photocathodes utilized for the generation of high brightness electron beams in superconducting radio frequency (SRF) photoinjector cavities. Operation at high field strength is required to obtain a low emittance beam, thus increasing the probability of field emission (FE) from the cathode surface. Usually, substrates are heated in situ before alkali deposition to remove oxide layers from the surface. FE onMo substrates was measured bymeans of a field emission scanning microscope (FESM). It turned out that in situ heat treatment (HT) of the Mo surface significantly changes the FE behaviour by activation of new emitters. For a better understanding of the mechanism for enhanced emission after in situ heating a witness Mo sample was investigated using x-ray photoelectron spectroscopy.
منابع مشابه
Mechano-chemical activation of MoO3-CuO/C powder mixture to synthesis nano crystalline Mo-Cu alloy
In this study, a high energy planetary ball milling technique was used to synthesize nano-crystalline Mo-Cu alloys. Molybdenum trioxide (MoO3) and copper oxide (CuO) were used as the starting materials. Carbo-thermal co-reduction of mixed Mo and Cu oxides powders was done with milling followed by a heat treatment at a high temperature. Differential thermal analysis/thermogravimetric (DTA/TG) wa...
متن کاملDeposition of Nano-Crystalline Fluor-hydroxyapatite Coatings on Titanium Substrates via Sol-Gel Method
In this investigation, fluor-hydroxyapatite (FHA) film was deposited on a titanium substrate by sol-gel method. Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as P, F and Ca precursors. Typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºC, the coating layers were ...
متن کاملOptical properties of spin-coated Er-doped Ga1As39S60 Chalcogenide thin films
Spin-coating of Chalcogenide glasses is a cost-effective and flexible method to produce thin films applicable in photonics. In this paper Er was doped into Ga1As39S60 glass by melt quenching technique and solutions for spin coating were prepared from glass powders dissolved in Propylamine and Ethylendiamine. Substrates used were microscopic slides (refractive index of about 1.51). Applied layer...
متن کاملOhmic Contact of Cu/Mo and Cu/Ti Thin Layers on Multi-Crystalline Silicon Substrates
Cu-Mo and Cu-Ti contact structures were fabricated on multi-crystalline silicon substrates to provide a low resistance ohmic contact. Deposition steps are done in an excellent vacuum chamber by means of electron beam evaporation and samples are then annealed for the realization of an efficient alloy layer. The effects of process parameters such as film thickness, annealing duration and temp...
متن کاملConductive Polythiophene Nanoparticles Deposition on Transparent PET Substrates: Effect of Modification with Hybrid Organic-inorganic Coating (RESEARCH NOTE)
In this work, Poly(ethyleneterephthalate) (PET) substrate was treated using KOH solution and was modified using hybrid O-I coating containing PCL )polycaprolactone( as organic phase and TEOS )tetraethoxysilane( as inorganic phase. The coating was prepared through a sol-gel process and applied on the surface by dip coater. Then, electrically conducting polythiophene (PTh) nanoparticles were depo...
متن کامل