Gilbert damping in CoFeB/GaAs(001) film with enhanced in-plane uniaxial magnetic anisotropy

A 3.5 nm amorphous CoFeB film was sputtered on GaAs (001) wafer substrate without applying magnetic field during deposition, and a significant in-plane uniaxial magnetic anisotropy (UMA) field (Hu) of about 300 Oe could be achieved. To precisely determine the intrinsic Gilbert damping constant (α) of this film, both ferromagnetic resonance (FMR) and time-resolved magneto-optical Kerr effect (TRMOKE) techniques were utilized. With good fitting of the dynamic spectra of FMR and TRMOKE, α is calculated to be 0.010 and 0.013, respectively. Obviously, the latter is 30% larger than the former, which is due to the transient heating effect during the TRMOKE measurement. In comparison with ordinary amorphous CoFeB films with negligible magnetic anisotropies, α is enhanced significantly in the CoFeB/GaAs(001) film, which may be mainly resulted from the enhanced spin-orbit coupling induced by the CoFeB/GaAs interface. However, the significant in-plane UMA plays minor role in the enhancement of α.