Cu1.94S-Assisted Growth of Wurtzite CuInS2 Nanoleaves by In Situ Copper Sulfidation
نویسندگان
چکیده
Wurtzite CuInS2 nanoleaves were synthesized by Cu1.94S-assisted growth. By observing the evolution of structures and phases during the growth process, Cu1.94S nanocrystals were found to be formed after uninterrupted oxidation and sulfidation of copper nanoparticles at the early stage, serving as catalysts to introduce the Cu and In species into CuInS2 nanoleaves growth for inherent property of fast ionic conductor. The obtained CuInS2 nanoleaves were characterized by scanning transmission electron microscopy, transmission electron microscopy, fast Fourier transform, X-ray diffraction, and energy dispersive X-ray spectroscopy mapping. The enhancement of photoresponsive current of CuInS2 nanoleaf film, evaluated by I-V curves of nanoleaf film, is believed to be attributed to the fast carrier transport benefit from the nature of single crystalline of CuInS2 nanoleaves.
منابع مشابه
Solution-based synthesis of wurtzite Cu2ZnSnS4 nanoleaves introduced by α-Cu2S nanocrystals as a catalyst.
Cu2ZnSnS4 is a promising solar absorbing material in solar cells due to its high absorption coefficient and abundance on earth. We have demonstrated that wurtzite Cu2ZnSnS4 nanoleaves could be synthesized through a facile solution-based method. Detailed investigation of the growth process indicates that α-Cu2S nanocrystals are first formed and then serve as a catalyst to introduce the Cu, Zn, a...
متن کاملSynthesis of hexagonal structured wurtzite and chalcopyrite CuInS2 via a simple solution route
Wurtzite semiconductor CuInS2 [CIS] has been reported in recent years. As a kind of metastable structure, it is a great challenge to synthesize pure wurtzite CIS at low temperature. In this paper, via a simple and quick solution route, we synthesize both wurtzite- and chalcopyrite-structure CIS. Well-controlled wurtzite CIS hexagonal plates are obtained when an appropriate agent is added. The i...
متن کاملThe phase transformation of CuInS2 from chalcopyrite to wurtzite
In the present work, CuInS2 nanoparticles have been successfully synthesized by water-bath method with deionized water as solvent and thioglycolic acid as complexing agent at 80°C. The phase transition of CuInS2 from chalcopyrite to wurtzite was realized by adjusting the pH value of reaction solution. The emergence of Cu2S in the condition of higher pH value of reaction solution led to the form...
متن کاملHighly Luminescent Water-Dispersible NIR-Emitting Wurtzite CuInS2/ZnS Core/Shell Colloidal Quantum Dots
Copper indium sulfide (CIS) quantum dots (QDs) are attractive as labels for biomedical imaging, since they have large absorption coefficients across a broad spectral range, size- and composition-tunable photoluminescence from the visible to the near-infrared, and low toxicity. However, the application of NIR-emitting CIS QDs is still hindered by large size and shape dispersions and low photolum...
متن کاملSolvothermal synthesis of zincblende and wurtzite CuInS2 nanocrystals and their photovoltaic application.
We report a simple solvothermal synthesis approach to the growth of CuInS(2) nanocrystals with zincblende- and wurtzite-phase structures. Zincblende nanocrystals with particle sizes of 10-20 nm were produced using oleylamine as the solvent. When ethylenediamine was used as the solvent, similarly sized wurtzite nanocrystals with some degree of particle aggregation were formed. Use of a mixture o...
متن کامل