We compare the methods of continuous solvent (Soxhlet) and supercritical solvent extractions for the removal of the organic template from nanostructured silica monoliths. Our monoliths are formed by templating the L3 liquid crystal phase of cetylpyridinium chloride in aqueous solutions with tetramethoxy silane. The monoliths that result from both Soxhlet and supercritical extraction methods are mechanically robust, optically clear, and free of cracks. The Soxhlet method compares favorably with supercritical solvent extraction in that equivalent L3-templated silica can be synthesized without the use of specialized reactor hardware or higher temperatures and high pressures, while avoiding noxious byproducts. The comparative effectiveness of various solvents in the Soxhlet process is related to the Hildebrand solubility parameter, determined by the effective surface area of the extracted silica.
منابع مشابه
Silica monoliths templated on L3 liquid crystal.
Dimensionally stable, optically clear, highly porous (approximately 65% of the apparent volume), and high surface area (up to 1400 m(2)/g) silica monoliths were fabricated as thick disks (0.5 cm) by templating the isotropic liquid crystalline L(3) phase with silica through the hydrolysis and condensation of a silicon alkoxide and then removing the organic constituents by supercritical ethanol e...
متن کاملThe stability of L3 sponge phase in acidic solutions.
In the synthesis of the disordered lyotropic liquid crystalline L3 sponge phase prepared with the cosurfactants cetylpyridinium chloride and hexanol, aqueous NaCl solution is used as the solvent. When this sponge phase is used as the template for L3 silica-phase processing, we replace NaCl with HCl to facilitate the acid catalysis of tetramethoxysilane in forming a templated silica gel, assumin...
متن کاملPercolation transition in the porous structure of latex-templated silica monoliths
Porous sol-gel silica monoliths are prepared using PMMA nanoparticles, 60 nm in diameter, as sacrificial templates. The pore-structure of the calcined pellets is investigated through nitrogen adsorption to assess the evolution of the porosity when varying the amount of porogen. The latex templated monoliths present a well defined spherical extrinsic porosity and an intrinsic microporosity due t...
متن کاملA Soft and Efficient Approach for Removal of Template from Mesoporous Silica using Benzene Sulfonamide
In this contribution, an effective and soft method for removal of template from nanochannels of mesoporous silica (MCM-41) is proposed. This method is based on chemically-modified solvent extraction which enhanced by means of an auxiliary organic compound, i.e. benzene sulfonamide. Template removal was performed in soft condition, i.e. in the presence of diluted sulfuric acid and at ambient tem...
متن کاملPreparation of mesoporous silica monoliths with ordered arrays of macrochannels templated from electric-field-oriented hydrogels.
The fabrication of ordered inorganic arrays of varying length scales and with multimodal porosities is of practical importance owing to their potential application in many areas of materials chemistry, including catalysis and separations science. A common approach to the controlled synthesis of this class of materials, first exploited in the synthesis of the MCM-41 family of molecular sieves, i...