Additive Manufacturing Laser Deposition of Ti-6Al-4V for Aerospace Repair Applications
نویسندگان
چکیده
Parts or products from high performance metal are very expensive, partly due to the processing complexities during manufacturing. The purpose of this project is to use additive laser deposition and machining processes to repair titanium parts, thus extending the service life of these parts. The study broadly included preparing the defects, laser deposition, machining, sample preparation and mechanical tests. Comparative study of mechanical properties (UTS, YS, percentage elongation) of the repaired samples to the ideal conditions was undertaken. The research throws up interesting facts where the data from the test sample shows enhancement of properties of the repaired part.
منابع مشابه
Data related to cyclic deformation and fatigue behavior of direct laser deposited Ti–6Al–4V with and without heat treatment
Data is presented describing the strain-controlled, fully-reversed uniaxial cyclic deformation and fatigue behavior of Ti-6Al-4V specimens additively manufactured via Laser Engineered Net Shaping (LENS) - a Direct Laser Deposition (DLD) process. The data was collected by performing multiple fatigue tests on specimens with various microstructural states/conditions, i.e. in their 'as-built', anne...
متن کاملInnovative Process Model of Ti-6al-4v Additive Layer Manufacturing Using Cold Metal Transfer (cmt)
New approaches to modern manufacture have emerged from Additive Layer Manufacturing (ALM) technologies over the last 25 years. These approaches provide form, fit and function to a wide range of metallic alloys and components. Wire + Arc Additive Layer Manufacture (WAALM) has gained the interest of the research community in recent years due to its high deposition rate and efficiency (100%). The ...
متن کاملHeat Treatment of Ti-6al-4v Produced by Lasercusing
LaserCUSING® is a selective laser melting (SLM) process that is capable of manufacturing parts by melting powder with heat input from a laser beam. LaserCUSING demonstrates potential for producing the intricate geometries specifically required for biomedical implants and aerospace applications. One main limitation to this form of rapid prototyping is the lack of published studies on the materia...
متن کاملAn Overview of Densification, Microstructure and Mechanical Property of Additively Manufactured Ti-6Al-4V — Comparison among Selective Laser Melting, Electron Beam Melting, Laser Metal Deposition and Selective Laser Sintering, and with Conventional Powder Metallurgy
This chapter begins with an introduction of the fundamental properties of Ti-6Al-4V, and its densification mechanism, typical microstructure and mechanical property achievable by conventional PM routes. This functions as a point of reference for the following discussion of the AM Ti-6Al-4V in terms of densification, microstructure, and mechanical property. The mostly popular laser-based AM tech...
متن کاملCorrigendum to “Experimental Study of Direct Laser Deposition of Ti-6Al-4V and Inconel 718 by Using Pulsed Parameters”
Laser direct metal deposition (LDMD) has developed from a prototyping to a single metal manufacturing tool. Its potential for creating multimaterial and functionally graded structures is now beginning to be explored. This work is a first part of a study in which a single layer of Inconel 718 is deposited on Ti-6Al-4V substrate. Single layer tracks were built at a range of powder mass flow rates...