Effect of Er,Cr:YSGG Laser at Different Output Powers on the Micromorphology and the Bond Property of Non-Carious Sclerotic Dentin to Resin Composites

BACKGROUND The objective of this study was to investigate the influence of Er,Cr:YSGG laser irradiated at different powers on the micromorphology and the bonding property of non-carious sclerotic dentin to resin composites. METHODS Two hundred bovine incisors characterized by non-carious sclerotic dentin were selected, and the seventy-two teeth of which for surface morphological analysis were divided into nine groups according to various treatments (A: the control group, B: only treated with the adhesive Adper Easy One, C: diamond bur polishing followed by Adper Easy One, D-I: Er,Cr:YSGG laser irradiating at 1W, 2W, 3W, 4W, 5W, 6W output power, respectively, followed by Adper Easy One). The surface roughness values were measured by the non-contact three-dimensional morphology scanner, then the surface micromorphologies of surfaces in all groups were assessed by scanning electron microscopy (SEM); meanwhile, Image Pro-Plus 6.0 software was used to measure the relative percentage of open tubules on SEM images. The rest, one hundred twenty-eight teeth for bond strength test, were divided into eight groups according to the different treatments (A: only treated with the adhesive Adper Easy One, B: diamond bur polishing followed by the above adhesive, C-H: Er,Cr:YSGG laser irradiating at 1 W, 2 W, 3 W, 4 W, 5 W, 6 W output power, respectively, followed by the above adhesive), and each group was subsequently divided into two subgroups according to whether aging is performed (immediately tested and after thermocycling). Micro-shear bond strength test was used to evaluate the bond strength. RESULTS The 4W laser group showed the highest roughness value (30.84±1.93μm), which was statistically higher than the control group and the diamond bur groups (p<0.05). The mean percentages ((27.8±1.8)%, (28.0±2.2)%, (30.0±1.9)%) of open tubules area in the 4W, 5W, 6W group were higher than other groups (p<0.05). The 4W laser group showed the highest micro-shear bond strength not only in immediately tested (17.60±2.55 PMa) but after thermocycling (14.35±2.08MPa). CONCLUSION The Er,Cr:YSGG laser at 4W power can effectively improve the bonding property between non-carious sclerotic dentin and resin composites by increasing the roughness and mean percentage area of open tubules.