Sustained release of rhBMP-2 from microporous tricalciumphosphate using hydrogels as a carrier.

نویسندگان

  • Steffen Kissling
  • Michael Seidenstuecker
  • Ingo H Pilz
  • Norbert P Suedkamp
  • Hermann O Mayr
  • Anke Bernstein
چکیده

BACKGROUND Tissue engineering and bone substitutes are subjects of intensive ongoing research. If the healing of bone fractures is delayed, osteoinductive materials that induce mesenchymal stem cells (MSCs) to form bone are necessary. The use of Bone Morphogenetic Protein - 2 is a common means to enhance effectiveness and accelerate the healing process. A delivery system that maintains and releases BMP biological activity in controlled fashion at the surgical site while preventing systemic diffusion (and thereby the risk of undesirable effects by controlling the amount of protein implanted) is essential. In this study, we aimed to test a cylindrical TCP-scaffold (porosity ~ 40 %, mean pore size 5 μm, high interconnectivity) in comparison to BMP-2. Recombinant human BMP-2 was dissolved in different hydrogels as a carrier, namely gelatin and alginate cross-linked with CaCl2-solution, or a solution of GDL and CaCO3. FITC-labeled Protein A was used as a model substance for rhBMP-2 in the pre-trials. For loading, the samples were put in a flow chamber and sealed with silicone rings. Using a directional vacuum, the samples were loaded with the alginate-BMP-2-mixture and the loading success monitored by observing changes in a fluorescent dye (FITC labeled Protein A) under a fluorescence microscope. A fluorescence reader and ELISA were employed to measure the release. Efficacy was determined in cell culture experiments (MG63 cells) via Live-Dead-Assay, FACS, WST-1-Assay, pNPP alkaline phosphatase assay and confocal microscopy. For statistical analysis, we calculated the mean and standard deviation and carried out an analysis of variance. RESULTS Directional vacuum makes it possible to load nearly 100 % of the interconnected micropores with alginate mixed with rhBMP-2. Using alginate hardened with CaCl2 as a carrier, BMP-2's release can be decelerated significantly longer than with other hydrogels - eg, for over 28 days. The effects on osteoblast-like cells were an increase of the growth rate and expression of alkaline phosphatase while triggering no toxic effect. CONCLUSION The rhBMP-2-loaded microporous TCP scaffolds possess proliferative and osteoinductive potential. Alginate helps to lower the local growth factor dose below the cytotoxic limit, and allows the release period to be lengthened by at least 28 days.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Mesoporous calcium–silicon xerogels with mesopore size and pore volume influence hMSC behaviors by load and sustained release of rhBMP-2

Mesoporous calcium-silicon xerogels with a pore size of 15 nm (MCS-15) and pore volume of 1.43 cm(3)/g were synthesized by using 1,3,5-mesitylene (TMB) as the pore-expanding agent. The MCS-15 exhibited good degradability with the weight loss of 50 wt% after soaking in Tris-HCl solution for 56 days, which was higher than the 30 wt% loss shown by mesoporous calcium-silicon xerogels with a pore si...

متن کامل

Analysis of hydrolyzable polyethylene glycol hydrogels and deproteinized bone mineral as delivery systems for glycosylated and non-glycosylated bone morphogenetic protein-2.

Bone morphogenetic proteins (BMP), in particular BMP-2, are the growth factors primarily responsible for osteoinduction. A knowledge of interactions between bone substitute materials and growth factor variants is crucial to designing bone substitutes with an ideal release profile. Here we compare glycosylated and non-glycosylated recombinant human bone morphogenetic protein-2 (rhBMP-2) either i...

متن کامل

Fabrication and release behavior of a novel freeze-gelled chitosan/gamma-PGA scaffold as a carrier for rhBMP-2.

OBJECTIVE The aim of this study was to fabricate a novel composite porous scaffold by blending chitosan and gamma-poly(glutamic acid) (gamma-PGA) for the sustained delivery of rhBMP-2. METHODS Chitosan and gamma-PGA were blended to fabricate a novel porous scaffold by the freeze-gelation method. For comparison, scaffolds made of freeze-dried chitosan, freeze-dried PLLA, and freeze-gelled chit...

متن کامل

Sustained release of VH and rhBMP-2 from nanoporous magnesium–zinc–silicon xerogels for osteomyelitis treatment and bone repair

Nanoporous magnesium-zinc-silicon (n-MZS) xerogels with a pore size ∼4 nm, a surface area of 718 cm(2)/g, and a pore volume of 1.24 cm(3)/g were synthesized by a sol-gel method. The n-MZS xerogels had high capacity to load vancomycin hydrochloride (VH) and human bone morphogenetic protein-2 (rhBMP-2), after soaking in phosphate buffered saline (PBS) for 24 hours (1.5 and 0.8 mg/g, respectively)...

متن کامل

Improving bone formation in a rat femur segmental defect by controlling bone morphogenetic protein-2 release.

Nonunion is a common complication in open fractures and other severe bone injuries. Recombinant human bone morphogenetic protein-2 (rhBMP-2) delivered on a collagen sponge enhances healing of fractures. However, the burst release of rhBMP-2 necessitates supra-physiological doses of rhBMP-2 to achieve a robust osteogenic effect, which introduces risk of ectopic bone formation and severe inflamma...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:
  • BMC biotechnology

دوره 16 1  شماره 

صفحات  -

تاریخ انتشار 2016